| Ticona CELANEX 3316 PBT, 30% Glass Reinforced | |||
|---|---|---|---|
| Categories: | Polymer; Thermoplastic; Polyester, TP; Polybutylene Terephthalate (PBT); Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled | ||
| Material Notes: | Celanex 3316 is a non-exuding flame retarded (UL and CSA approved V-0 at 1/32 inch and 5V at 1/16 inch), 30% fiberglass reinforced polybutylene terephthalate which has an excellent balance of mechanical properties and processability. It is well suited forTo avoid hydrolytic degradation during processing, CELANEX resins have to be dried to a moisture level equal to or less than 0.02%. Drying should be done in a dehumidifying hopper dryer capable of dewpoints <-40°F (-40°C) at 250°F (121°C) for 4 hours.For subsequent storage of the material in the dryer until processed (<= 60 h) it is necessary to lower the temperature to 100° C.
Information provided by Ticona | ||
| Key Words: | 30% glass-fiber, V-0, non-exuding | ||
| Vendors: | No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. | ||
| |||
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.66 g/cc | 1.66 g/cc | ASTM D792 |
| Density | 1.66 g/cc | 0.0600 lb/in³ | ISO 1183 |
| Water Absorption | 0.160 % | 0.160 % | 23°C/50%RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.00300 - 0.00500 cm/cm | 0.00300 - 0.00500 in/in | ASTM D955 |
| 0.00100 - 0.00800 cm/cm | 0.00100 - 0.00800 in/in | ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.00800 - 0.0130 cm/cm | 0.00800 - 0.0130 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 89.0 | 89.0 | ISO 2039-2 |
| Tensile Strength at Break | 135 MPa | 19600 psi | 5mm/min; ISO 527-2/1A |
| 134 MPa@Temperature 22.8 °C | 19500 psi@Temperature 73.0 °F | ASTM D638 | |
| Tensile Stress | 16.8 MPa@Strain 0.158 %,Temperature 23.0 °C | 2440 psi@Strain 0.158 %,Temperature 73.4 °F | |
| 33.5 MPa@Strain 0.316 %,Temperature 23.0 °C | 4860 psi@Strain 0.316 %,Temperature 73.4 °F | ||
| 49.1 MPa@Strain 0.474 %,Temperature 23.0 °C | 7120 psi@Strain 0.474 %,Temperature 73.4 °F | ||
| 62.7 MPa@Strain 0.632 %,Temperature 23.0 °C | 9090 psi@Strain 0.632 %,Temperature 73.4 °F | ||
| 74.5 MPa@Strain 0.790 %,Temperature 23.0 °C | 10800 psi@Strain 0.790 %,Temperature 73.4 °F | ||
| 84.8 MPa@Strain 0.948 %,Temperature 23.0 °C | 12300 psi@Strain 0.948 %,Temperature 73.4 °F | ||
| 93.2 MPa@Strain 1.11 %,Temperature 23.0 °C | 13500 psi@Strain 1.11 %,Temperature 73.4 °F | ||
| 100 MPa@Strain 1.26 %,Temperature 23.0 °C | 14500 psi@Strain 1.26 %,Temperature 73.4 °F | ||
| 106 MPa@Strain 1.42 %,Temperature 23.0 °C | 15400 psi@Strain 1.42 %,Temperature 73.4 °F | ||
| 110 MPa@Strain 1.58 %,Temperature 23.0 °C | 16000 psi@Strain 1.58 %,Temperature 73.4 °F | ||
| Elongation at Break | 2.50 % | 2.50 % | 5mm/min; ISO 527-2/1A |
| 2.50 %@Temperature 22.8 °C | 2.50 %@Temperature 73.0 °F | ASTM D638 | |
| Tensile Modulus | 10.7 GPa | 1550 ksi | 1mm/min; ISO 527-2/1A |
| 9.65 GPa@Temperature 22.8 °C | 1400 ksi@Temperature 73.0 °F | ASTM D638 | |
| Flexural Stiffness | 203 MPa@Temperature 22.8 °C | 29500 psi@Temperature 73.0 °F | ASTM D790 |
| Flexural Modulus | 10.3 GPa | 1490 ksi | ISO 178 |
| 9.65 GPa@Temperature 22.8 °C | 1400 ksi@Temperature 73.0 °F | ASTM D790 | |
| Flexural Strength | 200 MPa | 29000 psi | ISO 178 |
| Charpy Impact Unnotched | 5.90 J/cm² | 28.1 ft-lb/in² | ISO 179/1eU |
| 4.20 J/cm²@Temperature 30.0 °C | 20.0 ft-lb/in²@Temperature 86.0 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.850 J/cm² | 4.04 ft-lb/in² | ISO 179/1eA |
| 0.850 J/cm²@Temperature 30.0 °C | 4.04 ft-lb/in²@Temperature 86.0 °F | ISO 179/1eA | |
| Izod Impact, Notched | 0.747 J/cm@Temperature 22.8 °C | 1.40 ft-lb/in@Temperature 73.0 °F | ASTM D256 |
Celanex 5200
Celanex 5205HG
Celanex 5214HF
Celanex 5300-2
Celanex 5300-2UV
Celanex 531HS
Celanex 602AC
Celanex 6035GB20
Celanex 3209HRT
Celanex 3216
Celanex 3225HRT
Celanex 3226
Celanex 3300
Celanex 3300-2
Celanex 3300-2LM
Celanex 3300D
Celanex 3300HR
Celanex 3300LM
Celanex 3309HR
Celanex 3309HRHF
Celanex 3309HRLM
Celanex 3309HRT
Celanex 3316
Celanex 3316CT
Celanex 3318
Celanex 3325HRT
Celanex 3400-2
Celanex 3409HR
Celanex 3425HRT
Celanex 3016
Celanex 4022
Celanex 4202
Celanex 4300
Celanex 4300LM
Celanex 4302
Celanex 4302HS
Celanex 4302LM
Celanex 4305
Celanex 4306
Celanex 5200-2
Celanex 5200
Celanex 5205HG
Celanex 5214HF
Celanex 5300-2
Celanex 5300-2UV
Celanex 531HS
Celanex 602AC
Celanex 6035GB20
Celanex 3209HRT
Celanex 3216
Celanex 3225HRT
Celanex 3226
Celanex 3300
Celanex 3300-2
Celanex 3300-2LM
Celanex 3300D
Celanex 3300HR
Celanex 3300LM
Celanex 3309HR
Celanex 3309HRHF
Celanex 3309HRLM
Celanex 3309HRT
Celanex 3316
Celanex 3316CT
Celanex 3318
Celanex 3325HRT
Celanex 3400-2
Celanex 3409HR
Celanex 3425HRT
Celanex 3016
Celanex 4022
Celanex 4202
Celanex 4300
Celanex 4300LM
Celanex 4302
Celanex 4302HS
Celanex 4302LM
Celanex 4305
Celanex 4306
Celanex 5200-2
Celanex 3316 PBT特点：阻燃，30%的玻璃纤维增强，连接器。
处理方法：注塑成型。
应用范围：家用器具（食品加工刀片、真空吸尘器元件、电风扇、头发干燥机壳体、咖啡器皿等），电器元件（开关、电机壳、保险丝盒、计算机键盘按键等），汽车工业（散热器格窗、车身嵌板、车轮盖、门窗部件等）。（国际）塑胶贸易有限公司-Celanex PBT，可提供COC,SGS,物性表，等相关资料。
本公司主营产品：
一：泛用料：ABS、PP。
二：工程料：PC、PC/ABS、PA6、PA66、PA11、PA12、PA612、TPU、TPE、TPEE、TPV、LCP、PPS、PPO、PBT、PET、PMMA、POM等。
企业文化：“用劳动创造财富”；企业宗旨：“诚信经营，顾客至上”。
提 供：（国际）塑胶贸易有限公司
公司网址：
QQ：
塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。
2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家