| A3XZG5 Physical | Dry | Conditioned |
Unit
|
Test Method
|
|
Density
|
1.32
|
--
|
g/cm³
|
ISO 1183 |
|
Water Absorption
|
ISO 62 | |||
|
Saturation, 23°C
|
5.0
|
--
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
1.2
|
--
|
%
|
| A3XZG5 Mechanical | Dry | Conditioned |
Unit
|
Test Method
|
|
Tensile Modulus (23°C)
|
6500
|
4500
|
MPa
|
ISO 527-2 |
|
Tensile Stress (Break, 23°C)
|
105
|
70.0
|
MPa
|
ISO 527-2 |
|
Tensile Strain (Break, 23°C)
|
6.0
|
11
|
%
|
ISO 527-2 |
|
Flexural Modulus (23°C)
|
5500
|
--
|
MPa
|
ISO 178 |
| A3XZG5 Impact | Dry | Conditioned |
Unit
|
Test Method
|
|
Charpy Notched Impact Strength (23°C)
|
25
|
30
|
kJ/m²
|
ISO 179 |
|
Charpy Unnotched Impact Strength (23°C)
|
90
|
100
|
kJ/m²
|
ISO 179 |
| A3XZG5 Thermal | Dry | Conditioned |
Unit
|
Test Method
|
|
Heat Deflection Temperature
|
||||
|
0.45 MPa, Unannealed
|
250
|
--
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
240
|
--
|
°C
|
ISO 75-2/A |
|
Melting Temperature (DSC)
|
260
|
--
|
°C
|
ISO 3146 |
|
RTI Elec (1.50 mm)
|
120
|
--
|
°C
|
UL 746 |
|
RTI Imp (1.50 mm)
|
115
|
--
|
°C
|
UL 746 |
|
RTI Str (1.50 mm)
|
130
|
--
|
°C
|
UL 746 |
| A3XZG5 Electrical | Dry | Conditioned |
|
Test Method
|
|
Relative Permittivity (1 MHz)
|
3.80
|
--
|
|
IEC 60250 |
|
Dissipation Factor
|
||||
|
1 MHz
|
0.020
|
--
|
|
IEC 60250 |
|
1 MHz
|
--
|
0.030
|
|
IEC 60250 3 |
| A3XZG5 Flammability | Dry | Conditioned |
|
Test Method
|
|
Flame Rating (1.50 mm)
|
V-0
|
--
|
|
UL 94 |
| Injection |
Dry
|
Unit
|
|
|
Drying Temperature
|
80.0
|
°C
|
|
|
Drying Time
|
2.0 to 4.0
|
hr
|
|
|
Suggested Max Moisture
|
0.050
|
%
|
|
|
Processing (Melt) Temp
|
285 to 300
|
°C
|
|
|
Mold Temperature
|
80.0 to 90.0
|
°C
|
|
|
Injection Pressure
|
3.50 to 12.5
|
MPa
|
|
|
Injection Rate
|
Fast
|
|
|
| Injection Notes | |||
|
Product is supplied in sealed containers and drying prior to molding is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80 °C (176 °F) is recommended. Drying time is dependent on moisture level, but 2-4 hours is generally sufficient.
|
|||