| G1220物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
0.919
|
g/cm³
|
ASTM D792 |
|
熔流率 (190°C/2.16 kg)
|
2.0
|
g/10 min
|
ASTM D1238 |
| G1220薄膜 |
额定值
|
单位制
|
测试方法
|
|
膜耐刺穿性
|
Internal Method | ||
|
20 µm
|
7.20
|
J/cm³
|
|
|
51 µm
|
6.54
|
J/cm³
|
|
|
膜强度
|
ASTM D882 | ||
|
MD: 20 µm
|
87.6
|
J/cm³
|
|
|
MD: 51 µm
|
103
|
J/cm³
|
|
|
TD: 20 µm
|
83.5
|
J/cm³
|
|
|
TD: 51 µm
|
96.7
|
J/cm³
|
|
|
割线模量
|
ASTM D882 | ||
|
2% 正割, MD: 20 µm
|
176
|
MPa
|
|
|
2% 正割, MD: 51 µm
|
167
|
MPa
|
|
|
2% 正割, TD: 20 µm
|
207
|
MPa
|
|
|
2% 正割, TD: 51 µm
|
207
|
MPa
|
|
|
抗张强度
|
ASTM D882 | ||
|
MD: 屈服, 20 µm
|
10.1
|
MPa
|
|
|
MD: 屈服, 51 µm
|
10.2
|
MPa
|
|
|
TD: 屈服, 20 µm
|
10.3
|
MPa
|
|
|
TD: 屈服, 51 µm
|
10.6
|
MPa
|
|
|
MD: 断裂, 20 µm
|
30.6
|
MPa
|
|
|
MD: 断裂, 51 µm
|
27.4
|
MPa
|
|
|
TD: 断裂, 20 µm
|
21.2
|
MPa
|
|
|
TD: 断裂, 51 µm
|
23.0
|
MPa
|
|
|
伸长率
|
ASTM D882 | ||
|
MD: 断裂, 20 µm
|
570
|
%
|
|
|
MD: 断裂, 51 µm
|
720
|
%
|
|
|
TD: 断裂, 20 µm
|
660
|
%
|
|
|
TD: 断裂, 51 µm
|
740
|
%
|
|
|
落锤冲击
|
ASTM D1709A | ||
|
20 µm
|
76
|
g
|
|
|
51 µm
|
180
|
g
|
|
|
埃尔曼多夫抗撕强度 2
|
ASTM D1922 | ||
|
MD: 20 µm
|
91
|
g
|
|
|
MD: 51 µm
|
110
|
g
|
|
|
TD: 20 µm
|
310
|
g
|
|
|
TD: 51 µm
|
220
|
g
|
| G1220热性能 |
额定值
|
单位制
|
测试方法
|
|
维卡软化温度
|
96.7
|
°C
|
ASTM D1525 |
|
溶融温度（DSC）
|
116
|
°C
|
Internal Method |
| G1220光学性能 |
额定值
|
单位制
|
测试方法
|
|
光泽度
|
ASTM D2457 | ||
|
20°, 20.3 µm
|
86
|
|
|
|
20°, 50.8 µm
|
60
|
|
|
|
透明度
|
ASTM D1746 | ||
|
20.3 µm
|
94.0
|
|
|
|
50.8 µm
|
94.0
|
|
|
|
雾度
|
ASTM D1003 | ||
|
20.3 µm
|
7.4
|
%
|
|
|
50.8 µm
|
14
|
%
|
| G1220挤出 |
额定值
|
单位制
|
|
|
熔体温度
|
227
|
°C
|
|
| G1220挤压说明 | |||
|
吹塑薄膜的制造条件：
|
|||