| 5556物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
|||
|
--
|
1.20
|
g/cm³
|
ASTM D792 |
|
--
|
1.19
|
g/cm³
|
ISO 1183 |
|
熔流率
|
|||
|
220°C/2.16 kg
|
7.5
|
g/10 min
|
ASTM D1238 |
|
220°C/2.16 kg
|
8.1
|
g/10 min
|
ISO 1133 |
|
溶化体积流率（MVR） (220°C/2.16 kg)
|
7.00
|
cm³/10min
|
ISO 1133 |
|
收缩率
|
|||
|
流动
|
1.4
|
%
|
ASTM D955 |
|
横向流量: 2.00 mm
|
1.4
|
%
|
ISO 294-4 |
|
流量: 2.00 mm
|
1.4
|
%
|
ISO 294-4 |
|
吸水率
|
|||
|
23°C, 24 hr
|
0.50
|
%
|
ASTM D570 |
|
23°C, 24 hr
|
0.60
|
%
|
ISO 62 |
|
饱和, 23°C
|
0.60
|
%
|
ISO 62 |
|
平衡, 23°C, 50% RH
|
0.20
|
%
|
ISO 62 |
| 5556硬度 |
额定值
|
单位制
|
测试方法
|
|
硬度计硬度
|
|||
|
邵氏 D 3
|
55
|
|
ASTM D2240 |
|
邵氏 D 3
|
56
|
|
ISO 868 |
|
邵氏 D, 15 秒
|
51
|
|
ISO 868 |
| 5556机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量 (23°C)
|
180
|
MPa
|
ISO 527-2 |
|
抗张强度
|
|||
|
断裂, 23°C
|
40.0
|
MPa
|
ASTM D638, ISO 527-2/1BA |
|
5.0% 应变, 23°C
|
6.90
|
MPa
|
ASTM D638, ISO 527-2/1BA |
|
10% 应变, 23°C
|
10.3
|
MPa
|
ASTM D638 |
|
10% 应变, 23°C
|
11.0
|
MPa
|
ISO 527-2/1BA |
|
伸长率
|
|||
|
断裂, 23°C
|
500
|
%
|
ASTM D638 |
|
断裂, 23°C
|
480
|
%
|
ISO 527-2/1BA |
|
断张率 (23°C)
|
600
|
%
|
ISO 527-2/1BA |
|
拉伸蠕变模量
|
ISO 899-1 | ||
|
1 hr
|
170
|
MPa
|
|
|
1000 hr
|
133
|
MPa
|
|
|
弯曲模量
|
|||
|
-40°C
|
760
|
MPa
|
ASTM D790, ISO 178 |
|
23°C
|
207
|
MPa
|
ASTM D790 |
|
100°C
|
110
|
MPa
|
ASTM D790 |
|
23°C
|
190
|
MPa
|
ISO 178 |
|
100°C
|
100
|
MPa
|
ISO 178 |
| 5556冲击性能 |
额定值
|
单位制
|
测试方法
|
|
简支梁缺口冲击强度
|
ISO 179/1eA | ||
|
-40°C
|
150
|
kJ/m²
|
|
|
23°C
|
无断裂
|
|
|
|
简支梁缺口冲击强度
|
ISO 179/1eU | ||
|
-30°C
|
无断裂
|
|
|
|
23°C
|
无断裂
|
|
|
|
悬壁梁缺口冲击强度
|
|||
|
-40°C
|
170
|
J/m
|
ASTM D256 |
|
23°C
|
无断裂
|
|
ASTM D256, ISO 180/1A |
|
-40°C
|
无断裂
|
|
ISO 180/1A |
|
拉伸冲击强度 (23°C)
|
300
|
kJ/m²
|
ISO 8256 |
| 5556热性能 |
额定值
|
单位制
|
测试方法
|
|
热变形温度
|
|||
|
0.45 MPa, 未退火
|
90.0
|
°C
|
ASTM D648 |
|
0.45 MPa, 未退火
|
70.0
|
°C
|
ISO 75-2/B |
|
1.8 MPa, 未退火
|
49.0
|
°C
|
ASTM D648 |
|
1.8 MPa, 未退火
|
45.0
|
°C
|
ISO 75-2/A |
|
脆化温度
|
-95.0
|
°C
|
ISO 974 |
|
玻璃转化温度
|
-20.0
|
°C
|
ISO 11357-2 |
|
熔融温度
|
|||
|
-- 4
|
201
|
°C
|
ISO 11357-3 |
|
--
|
203
|
°C
|
ASTM D3418 |
|
线形膨胀系数
|
ASTM E831, ISO 11359-2 | ||
|
流动: -40 到 23°C
|
0.00016
|
cm/cm/°C
|
|
|
流动: 23 到 55°C
|
0.00018
|
cm/cm/°C
|
|
|
流动: 55 到 120°C
|
0.00019
|
cm/cm/°C
|
|
|
横向: -40 到 23°C
|
0.00017
|
cm/cm/°C
|
|
|
横向: 23 到 55°C
|
0.00018
|
cm/cm/°C
|
|
|
横向: 55 到 120°C
|
0.00018
|
cm/cm/°C
|
|
|
RTI Elec
|
UL 746 | ||
|
0.700 mm
|
85.0
|
°C
|
|
|
1.50 mm
|
85.0
|
°C
|
|
|
3.00 mm
|
85.0
|
°C
|
|
|
RTI Imp
|
UL 746 | ||
|
0.700 mm
|
50.0
|
°C
|
|
|
1.50 mm
|
85.0
|
°C
|
|
|
3.00 mm
|
85.0
|
°C
|
|
|
RTI Str
|
UL 746 | ||
|
0.700 mm
|
50.0
|
°C
|
|
|
1.50 mm
|
75.0
|
°C
|
|
|
3.00 mm
|
80.0
|
°C
|
| 5556电气性能 |
额定值
|
单位制
|
测试方法
|
|
表面电阻率
|
2.0E+15
|
ohm
|
IEC 60093 |
|
体积电阻率
|
4.0E+13
|
ohm·cm
|
IEC 60093 |
|
介电强度
|
|||
|
23°C, 1.91 mm 5
|
16
|
kV/mm
|
ASTM D149 |
|
23°C
|
19
|
kV/mm
|
IEC 60243-1 |
|
介电常数
|
|||
|
23°C, 1.91 mm, 100 Hz
|
4.60
|
|
ASTM D150 |
|
23°C, 1.91 mm, 1 kHz
|
4.50
|
|
ASTM D150 |
|
23°C, 1.91 mm, 1 MHz
|
4.10
|
|
ASTM D150 |
|
23°C, 100 Hz
|
4.80
|
|
IEC 60250 |
|
23°C, 1 MHz
|
4.40
|
|
IEC 60250 |
|
耗散因数
|
|||
|
23°C, 1.91 mm, 100 Hz
|
0.0060
|
|
ASTM D150 |
|
23°C, 1.91 mm, 1 kHz
|
0.0090
|
|
ASTM D150 |
|
23°C, 1.91 mm, 1 MHz
|
0.040
|
|
ASTM D150 |
|
23°C, 100 Hz
|
0.0090
|
|
IEC 60250 |
|
23°C, 1 MHz
|
0.038
|
|
IEC 60250 |
|
相比耐漏电起痕指数(CTI) (3.00 mm)
|
> 600
|
V
|
UL 746 |
|
漏电起痕指数
|
> 600
|
V
|
IEC 60112 |
| 5556可燃性 |
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级
|
UL 94, IEC 60695-11-10, -20 | ||
|
1.50 mm
|
HB
|
|
|
|
3.00 mm
|
HB
|
|
|
|
极限氧指数
|
20
|
%
|
ISO 4589-2 |
| 5556注射 |
额定值
|
单位制
|
|
|
干燥温度
|
100
|
°C
|
|
|
干燥时间 - 热风干燥机
|
2.0 到 3.0
|
hr
|
|
|
建议的最大水分含量
|
< 0.080
|
%
|
|
|
加工（熔体）温度
|
220 到 250
|
°C
|
|
|
Melt Temperature, Optimum - Injection Molding
|
230
|
°C
|
|
|
模具温度
|
45.0 到 55.0
|
°C
|
|
|
Mold Temperature, Optimum - Injection Molding
|
45
|
°C
|
|
|
Drying Recommended
|
Yes
|
|
|
| 5556挤出 |
额定值
|
单位制
|
|
|
干燥温度
|
100
|
°C
|
|
|
干燥时间
|
2.0 到 3.0
|
hr
|
|
|
建议的最大水分含量
|
< 0.060
|
%
|
|
|
熔体温度
|
220 到 235
|
°C
|
|
|
Extrusion Melt Temperature, Optimum
|
225
|
°C
|