2160 BK性能特点
|
|
|||
|
2160 BK用途
|
|
| 2160 BK物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
1.15
|
g/cm³
|
ASTM D792, ISO 1183 |
| 硬度 |
额定值
|
单位制
|
测试方法
|
|
硬度计硬度 (邵氏 A, 1.90 mm, 模压成型)
|
59
|
|
ASTM D2240, ISO 868 |
| 2160 BK弹性体 |
额定值
|
单位制
|
测试方法
|
|
拉伸应力
|
|||
|
100%应变
|
2.30
|
MPa
|
ASTM D412 |
|
100%应变, 1.90 mm
|
2.30
|
MPa
|
ISO 37 |
|
抗张强度 (断裂, 1.90 mm)
|
11.1
|
MPa
|
ASTM D412, ISO 37 |
|
伸长率
|
|||
|
断裂
|
620
|
%
|
ASTM D412 |
|
断裂, 1.90 mm
|
620
|
%
|
ISO 37 |
|
撕裂强度 3 (24°C)
|
55.0
|
kN/m
|
ASTM D624 |
|
压缩永久变形
|
ASTM D395, ISO 815 | ||
|
24°C, 22.0 hr
|
18
|
%
|
|
|
100°C, 22.0 hr
|
86
|
%
|
| 2160 BK热性能 |
额定值
|
单位制
|
测试方法
|
|
脆化温度
|
-68.0
|
°C
|
ASTM D746, ISO 812 |
| 补充信息 | |||
|
The value listed as Specific Gravity, ASTM D792, was tested in accordance with ASTM D471.
The value listed as Density, ISO 1183, was tested in accordance with ISO 2781. The value listed as Shore Hardness, ISO 868, was tested in accordance with ISO 48. Permanent Set (Tension), ASTM D412, Compression Molding, 1.9 mm: 14% 100% Modulus, ASTM D412, ISO 37, Physical Retention After 7 Days at 125°C, Compression Molding, 1.9 mm: 136% Tensile Strength, ASTM D412, ISO 37, DIN 53504, Physical Retention After 7 Days at 125°C, Compression Molding, 1.9 mm: 121% Elongation At Break, ASTM D412, ISO 37, Physical Retention After 7 Days at 125°C, Compression Molding, 1.9 mm: 103% Hardness, ISO 48, Physical Retention After 7 Days at 125°C, Shore A, Compression Molding, 1.9 mm: 55 Viscosity, ASTM D3835, 300 s-1 at 190°C, Compression Molding, 1.9 mm: 265 Pa*s Typical Processing Temperature, Compression Molding, 1.9 mm: 177° C Volume Change, ASTM D471, ISO 1817, After 7 days, 100°C, Water, Compression Molding, 1.9 mm: 6% Volume Change, After 7 days,ASTM D471, ISO 1817, 24°C, Fuel B, Compression Molding, 1.9 mm: 16% Volume Change, After 7 days, ASTM D471, ISO 1817, 100°C, ASTM #1 Oil, Compression Molding, 1.9 mm: -22% Volume Change, After 7 days, ASTM D471, ISO 1817, 100°C, IRM 903 Oil #3, Compression Molding, 1.9 mm: 4% Clash-Berg Stiffness Temperature, ASTM D1043, 10000 psi, Compression Molding, 1.9 mm: -49° C |