A chemically-crosslinkable MDPE compound for the production of high-flexible pipes for under floor heating application.
TA 1110 MD is a crosslinkable compound made by Silane grafted ethylene polymer. This graft polymer constitutes together with a Masterbatch containing the crosslinking catalyst a "SIOPLAS-SYSTEM". Pipes produced with the SILON grade TA 1110 MD fulfil the requirements of DIN 16894 and all related standards. This system allows the compound to be extruded as a normal thermoplastic polymer, which will attain a high level of crosslinking in the processed form. The final product has all the improved properties associated with crosslinked polyethylene. |
|
MDPE TABOREX TA 1110 MD 性能特点
|
|
|
MDPE TABOREX TA 1110 MD 用途
|
|
|
MDPE TABOREX TA 1110 MD 形式
|
|
|
MDPE TABOREX TA 1110 MD 加工方法
|
|
| MDPE TABOREX TA 1110 MD 物理性能 |
额定值
|
单位制
|
测试方法
|
|
密度
|
0.935
|
g/cm³
|
DIN 53479, ASTM D1505 |
|
表观密度
|
0.52
|
g/cm³
|
DIN 53466 |
|
熔流率 (190°C/5.0 kg)
|
3.3
|
g/10 min
|
Internal Method |
|
含水量
|
< 0.020
|
%
|
Internal Method |
|
挥发物
|
< 0.10
|
%
|
Internal Method |
|
凝胶含量 2
|
69
|
%
|
| MDPE TABOREX TA 1110 MD 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸应力 (断裂)
|
16.0
|
MPa
|
ISO 527-2 |
|
拉伸应变 (断裂)
|
150
|
%
|
ISO 527-2 |
| MDPE TABOREX TA 1110 MD 挤出 |
额定值
|
单位制
|
|
|
干燥温度
|
80.0 到 90.0
|
°C
|
|
|
干燥时间
|
2.0
|
hr
|
|
|
第1气缸区温度
|
160 到 170
|
°C
|
|
|
第2气缸区温度
|
170 到 180
|
°C
|
|
|
第3气缸区温度
|
170 到 190
|
°C
|
|
|
第4气缸区温度
|
170 到 190
|
°C
|
|
|
模具温度
|
190 到 220
|
°C
|
|
| 挤压说明 | |||
|
L/D: >25
Compression ratio: 3:1 to 2.5 : 1 Head: 200 to 210°C Screw: 70°C to 90 °C |
|||