PPS coolpoly d5108性能特点
|
|
|||
|
PPS coolpoly d5108形式
|
|
|||
|
PPS coolpoly d5108加工方法
|
|
| PPS coolpoly d5108物理性能 |
额定值
|
单位制
|
测试方法
|
|
密度
|
1.82
|
g/cm³
|
ISO 1183 |
|
收缩率
|
ASTM D955 | ||
|
流动
|
0.20
|
%
|
|
|
横向流动
|
0.40
|
%
|
| PPS coolpoly d5108机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
23600
|
MPa
|
ISO 527-2 |
|
拉伸应力 (屈服)
|
37.0
|
MPa
|
ISO 527-2 |
|
断张率
|
0.16
|
%
|
ISO 527-2 |
|
弯曲模量
|
19400
|
MPa
|
ISO 178 |
|
弯曲强度
|
69.0
|
MPa
|
ISO 178 |
| PPS coolpoly d5108冲击性能 |
额定值
|
单位制
|
测试方法
|
|
简支梁缺口冲击强度
|
1.1
|
kJ/m²
|
ISO 179 |
|
简支梁缺口冲击强度
|
2.5
|
kJ/m²
|
ISO 179 |
| PPS coolpoly d5108热性能 |
额定值
|
单位制
|
测试方法
|
|
热变形温度
|
|||
|
0.45 MPa, 未退火
|
276
|
°C
|
ISO 75-2/B |
|
1.8 MPa, 未退火
|
239
|
°C
|
ISO 75-2/A |
|
线形膨胀系数
|
ISO 11359-2 | ||
|
流动
|
6.5E-6
|
cm/cm/°C
|
|
|
横向
|
5.0E-6
|
cm/cm/°C
|
|
|
导热系数
|
10
|
W/m/K
|
ASTM C177 |
| PPS coolpoly d5108电气性能 |
额定值
|
单位制
|
测试方法
|
|
表面电阻率
|
4.5E+14
|
ohm
|
ASTM D257 |
|
体积电阻率
|
2.5E+16
|
ohm·cm
|
ASTM D257 |
|
介电强度
|
29
|
kV/mm
|
ASTM D149 |
|
介电常数
|
ASTM D150 | ||
|
100 Hz
|
4.80
|
|
|
|
1 MHz
|
3.70
|
|
|
|
耗散因数
|
ASTM D150 | ||
|
100 Hz
|
0.022
|
|
|
|
1 MHz
|
0.0023
|
|
|
|
耐电弧性
|
300
|
sec
|
ASTM D495 |
|
相比耐漏电起痕指数(CTI)
|
580
|
V
|
UL 746 |
|
热丝引燃 (HWI)
|
120
|
sec
|
UL 746 |
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级 (1.00 mm)
|
V-0
|
|
UL 94 |
| 补充信息 | |||
|
The value listed as Nominal Tensile Strain at Break, ISO 527-1, -2, was tested in accordance with ASTM D412.
The value listed as Thermal Conductivity, ASTM C177, was tested in accordance with ASTM E1461. The value listed as Mold Shrinkage, ASTM D955, was tested in accordance with ASTM D551. The value listed as Specific Heat ASTM C351, was tested in accordance with ASTM E1461. Thermal Diffusivity, ASTM E1461: 0.07 cm²/sec Comparative Tracking Index, ASTM 3638: 580 volts Hot Wire Ignition, ASTM D3874: >120 sec High Voltage Arc Tracking Rate, UL-746A: did not track High Voltage Arc Resistance to Ignition, UL-746A: >300 sec |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
150
|
°C
|
|
|
干燥时间
|
6.0
|
hr
|
|
|
Dew Point
|
-40.0
|
°C
|
|
|
建议的最大水分含量
|
0.0
|
%
|
|
|
螺筒后部温度
|
290 到 315
|
°C
|
|
|
螺筒中部温度
|
300 到 320
|
°C
|
|
|
螺筒前部温度
|
310 到 340
|
°C
|
|
|
射嘴温度
|
316 到 340
|
°C
|
|
|
加工（熔体）温度
|
307 到 338
|
°C
|
|
|
模具温度
|
135 到 177
|
°C
|
|
|
注塑温度
|
60.0 到 165
|
MPa
|
|
|
注射速度
|
中等偏快
|
|
|
|
保压
|
40.0 到 105
|
MPa
|
|
|
背压
|
0.200 到 0.500
|
MPa
|
|
|
螺杆转速
|
75 到 180
|
rpm
|
|
|
垫层
|
5.00 到 13.0
|
mm
|
|
|
螺杆压缩比
|
2.5:1.0
|
|