PA66 A3K Q601 低温特性佳

物性表：
Physical Properties	Metric	English	Comments
Density	1.13 g/cc	0.0408 lb/in³	ISO 1183
Moisture Absorption at Equilibrium	2.8 %	2.8 %	50% RH; ISO 62
	8.5 %	8.5 %	Saturation; ISO 62
Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	85.0 MPa	12300 psi	ISO 527
Elongation at Break	20 %	20 %	Nominal; ISO 527
Elongation at Yield	5.0 %	5.0 %	ISO 527
Tensile Modulus	3.00 GPa	435 ksi	ISO 527
Flexural Strength	100 MPa	14500 psi	ISO 178
Flexural Modulus	2.90 GPa	421 ksi	ISO 178
Izod Impact, Notched (ISO)	5.50 kJ/m² @Temperature 23.0 °C	2.62 ft-lb/in² @Temperature 73.4 °F	ISO 180
Charpy Impact Unnotched	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	ISO 179
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179
Charpy Impact, Notched	0.500 J/cm² @Temperature 23.0 °C	2.38 ft-lb/in² @Temperature 73.4 °F	ISO 179
Thermal Properties	Metric	English	Comments
Melting Point	260 °C	500 °F	ISO 3146
Deflection Temperature at 1.8 MPa (264 psi)	75.0 °C	167 °F	ISO 75
Processing Properties	Metric	English	Comments
Melt Temperature	280 - 300 °C	536 - 572 °F
Mold Temperature	40.0 - 80.0 °C	104 - 176 °F
Dry Time	2 - 4 hour	2 - 4 hour
Moisture Content	<= 0.20 %	<= 0.20 %
Descriptive Properties
Color	Q601
Commercial Status	North America

材料的密度1.30-1.40g/cm^3   一、性能指标: 外观 微黄色均匀颗粒              相对密度 1.30～1.40              含湿量(%) ≤1.5               拉伸强度(MPa) ≥150              静弯曲强度(MPa) ≥220              弯曲弹性模量(MPa) ≥6.5×103               缺口冲击强度(KJ/m2) ≥15 热变形温度(1.81MPa，℃) ≥210              玻璃纤维含量(%) 30±2  二、用途         本产品居于高强度、高耐热性、热胀系数和收缩率小，吸水性低，尺寸稳定性随大气湿度和温度变化而不大，它适合制作凸轮、伐座、收音机零部件、电子仪表零件、汽车交通零部件等。