PA66 FG42A NC010 低温特性佳

 PA66 FG42A NC010 尼龙中的主要品种是尼龙6和尼龙66，占绝对主导地位，其次是尼龙11，尼龙12，尼龙610，尼龙612，另外还有尼龙 1010，尼龙46，尼龙7，尼龙9，尼龙13，新品种有尼龙6I，尼龙9T和特殊尼龙MXD6（阻隔性树脂）等，尼龙的改性品种数量繁多，如增强尼龙，单体浇铸尼龙（MC尼龙），反应注射成型（RIM）

物性表：
Physical Properties	Metric	English	Comments
Density	1.01 g/cc	0.0365 lb/in³
	1.14 g/cc	0.0412 lb/in³	DAM; ISO 1183
Water Absorption	8.5 % @Thickness 2.00 mm	8.5 % @Thickness 0.0787 in	DAM; Sim. to ISO 62
Moisture Absorption	2.60 % @Thickness 2.00 mm	2.60 % @Thickness 0.0787 in	DAM; Sim. to ISO 62
Viscosity Test	280 cm³/g	280 cm³/g	DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow	0.014 cm/cm	0.014 in/in	DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse	0.014 cm/cm	0.014 in/in	DAM; ISO 294-4 2577
Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	55.0 MPa	7980 psi	50%RH; ISO 527-1/-2
	83.0 MPa	12000 psi	DAM; ISO 527-1/-2
Elongation at Break	>= 50 %	>= 50 %	DAM; Nominal; ISO 527-1/-2
	>= 50 %	>= 50 %	50%RH; Nominal; ISO 527-1/-2
Elongation at Yield	4.4 %	4.4 %	DAM; ISO 527-1/-2
	27 %	27 %	50%RH; ISO 527-1/-2
Tensile Modulus	1.30 GPa	189 ksi	50%RH; ISO 527-1/-2
	3.10 GPa	450 ksi	DAM; ISO 527-1/-2
Flexural Modulus	1.07 GPa	155 ksi	50%RH; ISO 178
	2.80 GPa	406 ksi	DAM; ISO 178
Izod Impact, Notched (ISO)	6.00 kJ/m²	2.86 ft-lb/in²	DAM; ISO 180/1A
	23.0 kJ/m²	10.9 ft-lb/in²	50%RH; ISO 180/1A
	6.00 kJ/m² @Temperature -30.0 °C	2.86 ft-lb/in² @Temperature -22.0 °F	50%RH; ISO 180/1A
	7.00 kJ/m² @Temperature -30.0 °C	3.33 ft-lb/in² @Temperature -22.0 °F	DAM; ISO 180/1A
Izod Impact, Unnotched (ISO)	NB	NB	DAM; ISO 180/1U
	NB	NB	50%RH; ISO 180/1U
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	DAM; ISO 180/1U
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	50%RH; ISO 180/1U
Charpy Impact Unnotched	NB	NB	DAM; ISO 179/1eU
	NB	NB	50%RH; ISO 179/1eU
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	DAM; ISO 179/1eU
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	50%RH; ISO 179/1eU
Charpy Impact, Notched	0.600 J/cm²	2.86 ft-lb/in²	DAM; ISO 179/1eA
	2.00 J/cm²	9.52 ft-lb/in²	50%RH; ISO 179/1eA
	0.400 J/cm² @Temperature -30.0 °C	1.90 ft-lb/in² @Temperature -22.0 °F	50%RH; ISO 179/1eA
	0.600 J/cm² @Temperature -30.0 °C	2.86 ft-lb/in² @Temperature -22.0 °F	DAM; ISO 179/1eA
Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+13 ohm-cm	1.00e+13 ohm-cm	50%RH; IEC 60093
	1.00e+15 ohm-cm	1.00e+15 ohm-cm	DAM; IEC 60093
Dielectric Constant	3.6 @Frequency 1.00e+6 Hz	3.6 @Frequency 1.00e+6 Hz	DAM; IEC 60250
	4.2 @Frequency 1.00e+6 Hz	4.2 @Frequency 1.00e+6 Hz	50%RH; IEC 60250
	4.3 @Frequency 100 Hz	4.3 @Frequency 100 Hz	DAM; IEC 60250
	10 @Frequency 100 Hz	10 @Frequency 100 Hz	50%RH; IEC 60250
Dielectric Strength	31.0 kV/mm	787 kV/in	DAM; IEC 60243-1
Dissipation Factor	0.015 @Frequency 1.00e+6 Hz	0.015 @Frequency 1.00e+6 Hz	DAM; IEC 60250
	0.015 @Frequency 100 Hz	0.015 @Frequency 100 Hz	DAM; IEC 60250
	0.075 @Frequency 1.00e+6 Hz	0.075 @Frequency 1.00e+6 Hz	50%RH; IEC 60250
	0.20 @Frequency 100 Hz	0.20 @Frequency 100 Hz	50%RH; IEC 60250
Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	100 µm/m-°C	55.6 µin/in-°F	DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow	100 µm/m-°C	55.6 µin/in-°F	DAM; ISO 11359-1/-2
Specific Heat Capacity	2.79 J/g-°C	0.667 BTU/lb-°F
Thermal Conductivity	0.160 W/m-K	1.11 BTU-in/hr-ft²-°F	of melt
Melting Point	262 °C	504 °F	DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	200 °C	392 °F	DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	70.0 °C	158 °F	DAM; ISO 75-1/-2
Vicat Softening Point	244 °C	471 °F	DAM; 50°C/h 50N; ISO 306
Glass Transition Temp, Tg	70.0 °C	158 °F	DAM; 10°C/min; ISO 11357-1/-2
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	DAM; IEC 60695-11-10
	V-2 @Thickness 3.00 mm	V-2 @Thickness 0.118 in	DAM; IEC 60695-11-10
Oxygen Index	28 %	28 %	DAM; ISO 4589-1/-2
Descriptive Properties
Additives	Release agent
Delivery form	Pellets
Part Marking Code	>PA66<	ISO 11469
Processing	Casting
	Coatable
	Film Extrusion
	Injection Moulding
	Other Extrusion
	Profile Extrusion
	Sheet Extrusion
Regional Availability	Europe
	Near East/Africa
	North America
	South and Central America
Resin Identification	PA66
UL recognition	UL	DAM
	UL	DAM

包括脂肪族PA，脂肪—芳香族PA和芳香族PA。其中，脂肪族PA品种多，产量大，应用广泛，其命名由合成单体具体的碳原子数而定。是美国著名化学家卡罗瑟斯和他的科研小组发明的。