TPV 3111-70A 物性表：
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 70 | 70 | ASTM D2240 | ||
| 60 @Treatment Temp. 140 °C, Time 3.629e+6 sec |
60 @Treatment Temp. 284 °F, Time 1008 hour |
heat aging; ASTM D573-99 | |||
| 67 @Treatment Temp. 120 °C, Time 3.629e+6 sec |
67 @Treatment Temp. 248 °F, Time 1008 hour |
heat aging; ASTM D573-99 | |||
| 75 @Treatment Temp. 100 °C, Time 3.60e+6 sec |
75 @Treatment Temp. 212 °F, Time 1000 hour |
water immersion | |||
| Tensile Strength | 15.0 MPa | 2180 psi | ASTM D412 | ||
| 8.85 MPa @Treatment Temp. 140 °C, Time 3.629e+6 sec |
1280 psi @Treatment Temp. 284 °F, Time 1008 hour |
heat aging; ASTM D573-99 | |||
| 11.25 MPa @Treatment Temp. 100 °C, Time 3.60e+6 sec |
1632 psi @Treatment Temp. 212 °F, Time 1000 hour |
water immersion | |||
| 12.15 MPa @Treatment Temp. 120 °C, Time 3.629e+6 sec |
1762 psi @Treatment Temp. 248 °F, Time 1008 hour |
heat aging; ASTM D573-99 | |||
| Elongation at Break | 600 % | 600 % | ASTM D412 | ||
| 378 % @Treatment Temp. 140 °C, Time 3.629e+6 sec |
378 % @Treatment Temp. 284 °F, Time 1008 hour |
heat aging; ASTM D573-99 | |||
| 480 % @Treatment Temp. 100 °C, Time 3.60e+6 sec |
480 % @Treatment Temp. 212 °F, Time 1000 hour |
water immersion | |||
| 702 % @Treatment Temp. 120 °C, Time 3.629e+6 sec |
702 % @Treatment Temp. 248 °F, Time 1008 hour |
heat aging; ASTM D573-99 | |||
| Compression Set | 20 % @Temperature 23.0 °C, Time 79200 sec |
20 % @Temperature 73.4 °F, Time 22.0 hour |
ASTM D395 | ||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 170 °C | 338 °F | extrusion | ||
| 180 °C | 356 °F | injection | |||
| Nozzle Temperature | 205 °C | 401 °F | |||
| Adapter Temperature | 190 °C | 374 °F | |||
| Die Temperature | 190 °C | 374 °F | |||
| Melt Temperature | 190 °C | 374 °F | extrusion | ||
| 205 °C | 401 °F | injection | |||
| Mold Temperature | 10.0 - 30.0 °C | 50.0 - 86.0 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Moisture Content | <= 0.030 % | <= 0.030 % | |||
| Back Pressure | 0.350 MPa | 50.8 psi | |||
| De |
|||||
| Injection Speed | fast |
||||
加工成品后物性优势：
1、 优异的抗老化性能和良好的耐候、耐热性能；
2、 优异的抗永久变形性能；
3、 优异的抗张强度、高韧性和高回弹性；
4、 优异的环保性能和可重复使用；
5、 优异的电绝缘性能；
6、 硬度范围广泛；
7、 使用温度范围广泛；
8、 颜色多样化，有全透明、半透明、浅色系列，着色容易，容易加工成型；
9、 可与PP、PA、PC、ABS、PS、PBT、PET等多种材料共注射或挤出成型。
广泛应用于：电子产品外壳及外保护、建筑材料密封条、交通器材缓冲部件、消费品的主体如鱼竿牙刷吸管、各种管道管件等、、、、
上海松翰塑化科技有限公司供应产品，品质一流，TPV种类齐全。 公司理念你的要求就是我们的追求 。咨询人夏先生 电话：13751253137 QQ：205730283 我公司将给你最专业产品加工工艺指导及帮你解决加工工艺难题 欢迎你的咨询
1、 优异的抗老化性能和良好的耐候、耐热性能；
2、 优异的抗永久变形性能；
3、 优异的抗张强度、高韧性和高回弹性；
4、 优异的环保性能和可重复使用；
5、 优异的电绝缘性能；
6、 硬度范围广泛；
7、 使用温度范围广泛；
8、 颜色多样化，有全透明、半透明、浅色系列，着色容易，容易加工成型；
9、 可与PP、PA、PC、ABS、PS、PBT、PET等多种材料共注射或挤出成型。
广泛应用于：电子产品外壳及外保护、建筑材料密封条、交通器材缓冲部件、消费品的主体如鱼竿牙刷吸管、各种管道管件等、、、、
上海松翰塑化科技有限公司供应产品，品质一流，TPV种类齐全。 公司理念你的要求就是我们的追求 。咨询人夏先生 电话：13751253137 QQ：205730283 我公司将给你最专业产品加工工艺指导及帮你解决加工工艺难题 欢迎你的咨询