PA6 HPN9350 性状为半透明或不透明乳白色结晶形聚合物，具有可塑性。密度1．15g／cm3。熔点252℃。脆化温度-30℃。热分解温度大于350℃。连续耐热80-120℃,平衡吸水率2．5％。能耐酸、碱、大多数无机盐水溶液、卤代烷、烃类、酯类、酮类等腐蚀，但易溶于苯酚、甲酸等极性溶剂。具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差。

颗粒：

、

物性表:

Physical Properties	Metric	English	Comments

Density	1.06 g/cc	0.0383 lb/in³	ISO 1183
Water Absorption	6.8 %	6.8 %	ISO 62
Moisture Absorption at Equilibrium	1.9 %	1.9 %	23°C/50% R.H.; ISO 62
Linear Mold Shrinkage	0.013 cm/cm	0.013 in/in	ASTM Data; MD

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	80	80	ASTM Test
Tensile Strength, Yield	45.0 MPa	6530 psi	50mm/min; ISO 527
	50.0 MPa	7250 psi	2 in/min; ASTM Test
Elongation at Break	>= 50 %	>= 50 %	50mm/min, Nominal strain; ISO 527
	>= 100 %	>= 100 %	2 in/min; ASTM Test
Elongation at Yield	4.5 %	4.5 %	50mm/min; ISO 527
	5.0 %	5.0 %	2 in/min; ASTM Test
Tensile Modulus	1.70 GPa	247 ksi	1mm/min; ISO 527
Flexural Strength	50.0 MPa	7250 psi	ISO Data
	69.0 MPa	10000 psi	ASTM Test
	9.50 MPa @Temperature 120 °C	1380 psi @Temperature 248 °F	ASTM Test
	10.0 MPa @Temperature 93.0 °C	1450 psi @Temperature 199 °F	ASTM Test
	15.0 MPa @Temperature 65.0 °C	2180 psi @Temperature 149 °F	ASTM Test
	105 MPa @Temperature -40.0 °C	15200 psi @Temperature -40.0 °F	ASTM Test
Flexural Modulus	1.45 GPa	210 ksi	ISO Data
	1.73 GPa	251 ksi	ASTM Test
	0.190 GPa @Temperature 120 °C	27.6 ksi @Temperature 248 °F	ASTM Test
	0.220 GPa @Temperature 93.0 °C	31.9 ksi @Temperature 199 °F	ASTM Test
	0.375 GPa @Temperature 65.0 °C	54.4 ksi @Temperature 149 °F	ASTM Test
Izod Impact, Notched	5.90 J/cm @Thickness 3.17 mm	11.1 ft-lb/in @Thickness 0.125 in	ASTM Test
Charpy Impact Unnotched	NB	NB	ISO 179
Charpy Impact, Notched	4.00 J/cm²	19.0 ft-lb/in²	ISO 179
	0.900 J/cm² @Temperature -30.0 °C	4.28 ft-lb/in² @Temperature -22.0 °F	ISO 179

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	10 K/min
	220 °C	428 °F	ASTM Test
Deflection Temperature at 1.8 MPa (264 psi)	50.0 °C	122 °F	ISO 75
	55.0 °C	131 °F	ASTM Test

Descriptive Properties
Color	Natural
Commercial Status	Active America
Form	Pellets
Impact Modified	Yes
Primary Processing Technique	Extrusion
Processing	Profile Extrusion
	Sheet extrusion
Special characteristic	Heat stabilized or stable to heat
UL.UL-C	Yes

广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。