颗粒：
、
、物性表:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | dry; ISO 1183 |
| Water Absorption | 6.5 % | 6.5 % | Sim. To ISO 62 |
| Moisture Absorption | 2.00 % | 2.00 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | cond; ISO 527-1/-2 |
| 80.0 MPa | 11600 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 3.0 % | 3.0 % | dry; ISO 527-1/-2 |
| 15 % | 15 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 2.50 GPa | 363 ksi | cond; ISO 527-1/-2 |
| 5.70 GPa | 827 ksi | dry; ISO 527-1/-2 | |
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
cond; ISO 179/1eU |
| 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eU | |
| 4.60 J/cm² @Temperature 23.0 °C |
21.9 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eU | |
| 9.30 J/cm² @Temperature 23.0 °C |
44.3 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eU | |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
cond; ISO 179/1eA |
| 0.400 J/cm² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA | |
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eA | |
| 0.900 J/cm² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | cond; IEC 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | dry; IEC 60093 | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | cond; IEC 60093 |
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
dry; IEC 60250 |
| 3.9 @Frequency 1.00e+6 Hz |
3.9 @Frequency 1.00e+6 Hz |
cond; IEC 60250 | |
| 4.3 @Frequency 100 Hz |
4.3 @Frequency 100 Hz |
dry; IEC 60250 | |
| 10 @Frequency 100 Hz |
10 @Frequency 100 Hz |
cond; IEC 60250 | |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | cond; IEC 60243-1 |
| 30.0 kV/mm | 762 kV/in | dry; IEC 60243-1 | |
| Dissipation Factor | 0.013 @Frequency 100 Hz |
0.013 @Frequency 100 Hz |
dry; IEC 60250 |
| 0.021 @Frequency 1.00e+6 Hz |
0.021 @Frequency 1.00e+6 Hz |
dry; IEC 60250 | |
| 0.10 @Frequency 1.00e+6 Hz |
0.10 @Frequency 1.00e+6 Hz |
cond; IEC 60250 | |
| 0.30 @Frequency 100 Hz |
0.30 @Frequency 100 Hz |
cond; IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | cond; IEC 60112 |
| 600 V | 600 V | dry; IEC 60112 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | dry; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | dry; ISO 75-1/-2 |
| Flammability, UL94 | V-2 @Thickness 1.50 mm |
V-2 @Thickness 0.0591 in |
dry; IEC 60695-11-10 |
| V-2 @Thickness 0.800 mm |
V-2 @Thickness 0.0315 in |
dry; IEC 60695-11-10 | |
| Glow Wire Test | 960 °C @Thickness 1.60 mm |
1760 °F @Thickness 0.0630 in |
Glow Wire Flammability Index, dry; IEC 60695-2-12 |
| 960 °C @Thickness 1.00 mm |
1760 °F @Thickness 0.0394 in |
Glow Wire Flammability Index, dry; IEC 60695-2-12 |
|
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。