| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | DAM; ISO 1183 | ||
| Water Absorption | 5.6 % @Thickness 2.00 mm |
5.6 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 | ||
| Moisture Absorption | 1.60 % @Thickness 2.00 mm |
1.60 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 | ||
| Viscosity Test | 150 cm³/g | 150 cm³/g | DAM; ISO 307 1157 1628 | ||
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | DAM; ISO 294-4 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | DAM; ISO 294-4 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | 50%RH; ISO 527-1/-2 | ||
| 140 MPa | 20300 psi | DAM; ISO 527-1/-2 | |||
| Elongation at Break | 3.0 % | 3.0 % | DAM; ISO 527-1/-2 | ||
| 6.0 % | 6.0 % | 50%RH; ISO 527-1/-2 | |||
| Tensile Modulus | 4.60 GPa | 667 ksi | 50%RH; ISO 527-1/-2 | ||
| 8.30 GPa | 1200 ksi | DAM; ISO 527-1/-2 | |||
| 2.75321 GPa @Temperature 170 °C |
399.320 ksi @Temperature 338 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| 3.67635 GPa @Temperature 110 °C |
533.210 ksi @Temperature 230 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| 8.359 GPa @Temperature 30.0 °C |
1212 ksi @Temperature 86.0 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| 8.37733 GPa @Temperature -20.0 °C |
1215.03 ksi @Temperature -4.00 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| 8.419 GPa @Temperature -70.0 °C |
1221 ksi @Temperature -94.0 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| 8.483 GPa @Temperature -100 °C |
1230 ksi @Temperature -148 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| Shear Modulus | 1.353 GPa @Temperature 100 °C |
196.2 ksi @Temperature 212 °F |
DAM; Dynamic; ISO 11403-1 -2 | ||
| 2.524 GPa @Temperature 60.0 °C |
366.1 ksi @Temperature 140 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| 2.914 GPa @Temperature 10.0 °C |
422.6 ksi @Temperature 50.0 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| 2.922 GPa @Temperature -40.0 °C |
423.8 ksi @Temperature -40.0 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| 2.931 GPa @Temperature -70.0 °C |
425.1 ksi @Temperature -94.0 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| 2.954 GPa @Temperature -100 °C |
428.4 ksi @Temperature -148 °F |
DAM; Dynamic; ISO 11403-1 -2 | |||
| Izod Impact, Notched (ISO) | 5.50 kJ/m² | 2.62 ft-lb/in² | DAM; ISO 180/1A | ||
| 9.00 kJ/m² | 4.28 ft-lb/in² | 50%RH; ISO 180/1A | |||
| 4.00 kJ/m² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 180/1A | |||
| 5.50 kJ/m² @Temperature -30.0 °C |
2.62 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 180/1A | |||
| Charpy Impact Unnotched | 6.00 J/cm² | 28.6 ft-lb/in² | DAM; ISO 179/1eU | ||
| 6.50 J/cm² | 30.9 ft-lb/in² | 50%RH; ISO 179/1eU | |||
| 5.00 J/cm² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 179/1eU | |||
| 5.00 J/cm² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | DAM; ISO 179/1eA | ||
| 1.20 J/cm² | 5.71 ft-lb/in² | 50%RH; ISO 179/1eA | |||
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
50%RH; ISO 179/1eA | |||
| 0.550 J/cm² @Temperature -30.0 °C |
2.62 ft-lb/in² @Temperature -22.0 °F |
DAM; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | DAM; IEC 60093 | ||
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | 50%RH; IEC 60093 | ||
| Dielectric Strength | 33.0 kV/mm | 838 kV/in | DAM; IEC 60243-1 | ||
| Dissipation Factor | 0.0038 @Frequency 1.00e+6 Hz |
0.0038 @Frequency 1.00e+6 Hz |
DAM; IEC 60250 | ||
| 0.013 @Frequency 100 Hz |
0.013 @Frequency 100 Hz |
DAM; IEC 60250 | |||
| Comparative Tracking Index | 500 V | 500 V | DAM; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 41.0 µm/m-°C | 22.8 µin/in-°F | DAM; ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 77.0 µm/m-°C | 42.8 µin/in-°F | DAM; ISO 11359-1/-2 | ||
| Specific Heat Capacity | 2.07 J/g-°C | 0.495 BTU/lb-°F | |||
| Thermal Conductivity | 0.230 W/m-K | 1.60 BTU-in/hr-ft²-°F | of melt | ||
| Melting Point | 221 °C | 430 °F | DAM; 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | DAM; ISO 75-1/-2 | ||
| Vicat Softening Point | 210 °C | 410 °F | DAM; 50°C/h 50N; ISO 306 | ||
| Glass Transition Temp, Tg | 70.0 °C | 158 °F | DAM; 10°C/min; ISO 11357-1/-2 | ||
| Flame Spread | 55 mm/min @Thickness 1.00 mm |
2.2 in/min @Thickness 0.0394 in |
ISO 3795 (FMVSS 302) | ||
| De |
|||||
| Additives | Release agent | ||||
| Delivery form | Pellets | ||||
| Part Marking Code | >PA6-(MD+GF)40< | ISO 11469 | |||
| Processing | Injection Moulding | ||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | PA6-(MD+GF)40 | ||||
| Special characteristics | Heat stabilised or stable to heat | ||||
| Platable | |||||
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636
QQ ：205730283
邮 箱 ：205730283@qq.com