颗粒：
、
、物性表:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.014 - 0.018 cm/cm | 0.014 - 0.018 in/in | on Tensile Bar; ISO 294 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 115 | 115 | ISO 2039-2 |
| Tensile Strength, Yield | 56.0 MPa | 8120 psi | 50 mm/min; ISO 527 |
| Elongation at Break | >= 100 % | >= 100 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.50 GPa | 363 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 80.0 MPa | 11600 psi | yield, 2 mm/min; ISO 178 |
| Flexural Modulus | 2.00 GPa | 290 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature -40.0 °C |
3.33 ft-lb/in² @Temperature -40.0 °F |
Edgew 80x10x4 sp=62; ISO 180/1A |
| 9.00 kJ/m² @Temperature -20.0 °C |
4.28 ft-lb/in² @Temperature -4.00 °F |
Edgew 80x10x4 sp=62; ISO 180/1A | |
| 13.0 kJ/m² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
Edgew 80x10x4 sp=62; ISO 180/1A | |
| Charpy Impact Unnotched | >= 10.0 J/cm² | >= 47.6 ft-lb/in² | Edgew 80x10x4 sp=62; ISO 179/1eU |
| Electrical Properties | Metric | English | Comments |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| 600 V | 600 V | M; IEC 60112 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 93.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
51.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 117 µm/m-°C @Temperature 23.0 - 60.0 °C |
65.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C | 171 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Af |
| Vicat Softening Point | 210 °C | 410 °F | B/120; ISO 306 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 220 - 230 °C | 428 - 446 °F | Zone 1 |
| Middle Barrel Temperature | 230 - 240 °C | 446 - 464 °F | Zone 2 |
| Front Barrel Temperature | 240 - 250 °C | 464 - 482 °F | Zone 3 |
| Melt Temperature | 240 - 250 °C | 464 - 482 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 75.0 - 85.0 °C | 167 - 185 °F | |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |
| Moisture Content | 0.20 % | 0.20 % | |
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：