物性表:
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | |||
| Linear Mold Shrinkage, Flow | 0.00850 - 0.0110 cm/cm | 0.00850 - 0.0110 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.00600 - 0.00800 cm/cm | 0.00600 - 0.00800 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 45.0 MPa @Temperature 60.0 °C |
6530 psi @Temperature 140 °F |
|||
| 70.0 MPa @Temperature 23.0 °C |
10200 psi @Temperature 73.4 °F |
||||
| Elongation at Break | 10.0 % @Temperature 23.0 °C |
10.0 % @Temperature 73.4 °F |
|||
| 60.0 % @Temperature 60.0 °C |
60.0 % @Temperature 140 °F |
||||
| >= 100 % @Temperature 90.0 °C |
>= 100 % @Temperature 194 °F |
||||
| >= 100 % @Temperature 120 °C |
>= 100 % @Temperature 248 °F |
||||
| >= 100 % @Temperature 150 °C |
>= 100 % @Temperature 302 °F |
||||
| Elongation at Yield | 3.00 % | 3.00 % | |||
| Tensile Modulus | 0.650 GPa @Temperature 150 °C |
94.3 ksi @Temperature 302 °F |
|||
| 0.850 GPa @Temperature 120 °C |
123 ksi @Temperature 248 °F |
||||
| 1.10 GPa @Temperature 90.0 °C |
160 ksi @Temperature 194 °F |
||||
| 2.00 GPa @Temperature 60.0 °C |
290 ksi @Temperature 140 °F |
||||
| 3.40 GPa @Temperature 23.0 °C |
493 ksi @Temperature 73.4 °F |
||||
| Charpy Impact Unnotched | 9.00 J/cm² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
|||
| 9.00 J/cm² @Temperature -20.0 °C |
42.8 ft-lb/in² @Temperature -4.00 °F |
||||
| Charpy Impact, Notched | 0.250 J/cm² @Temperature -20.0 °C |
1.19 ft-lb/in² @Temperature -4.00 °F |
|||
| 0.300 J/cm² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
||||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 600 V | 600 V | A solution | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 100 °C | 212 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | |||
| Vicat Softening Point | 210 °C @Load 5.00 kg |
410 °F @Load 11.0 lb |
|||
| Flammability, UL94 | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
|||
| V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
||||
| V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
||||
| Oxygen Index | 30.0 % | 30.0 % | |||
| Glow Wire Test | 960 °C @Thickness 1.00 mm |
1760 °F @Thickness 0.0394 in |
GWFI/GWT | ||
| 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
GWFI/GWT | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 245 - 260 °C | 473 - 500 °F | |||
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |||
| Drying Temperature | 90.0 - 100 °C @Time 10800 sec |
194 - 212 °F @Time 3.00 hour |
|||
| De |
|||||
| ISO Shrinkage - Pressure | 60 MPa | ||||