| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | ASTM D792 |
| Water Absorption | 1.0 % | 1.0 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0090 - 0.013 cm/cm @Thickness 3.20 mm |
0.0090 - 0.013 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 117 | 117 | ASTM D785 |
| Tensile Strength, Yield | 68.6 MPa @Thickness 3.20 mm |
9960 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Elongation at Break | 12 % @Thickness 3.20 mm |
12 % @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Flexural Yield Strength | 98.1 MPa @Thickness 3.20 mm |
14200 psi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
| Flexural Modulus | 3.92 GPa @Thickness 3.20 mm |
569 ksi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 22.0 kV/mm @Thickness 1.00 mm |
559 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Arc Resistance | 185 sec | 185 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 55.0 µm/m-°C | 30.6 µin/in-°F | ASTM D696 |
| Melting Point | 220 °C | 428 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C @Thickness 6.40 mm |
374 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C @Thickness 6.40 mm |
230 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 240 - 270 °C | 464 - 518 °F | Injection Molding |
| Middle Barrel Temperature | 245 - 275 °C | 473 - 527 °F | Injection Molding |
| Front Barrel Temperature | 245 - 275 °C | 473 - 527 °F | Injection Molding |
| Nozzle Temperature | 250 - 280 °C | 482 - 536 °F | Injection Molding |
| Melt Temperature | 250 - 280 °C | 482 - 536 °F | Injection Molding |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。