PA6 B3M6 30%矿物 PA6 、_产品资讯

PA6 B3M6 性状为半透明或不透明乳白色结晶形聚合物，具有可塑性。密度1．15g／cm3。熔点252℃。脆化温度-30℃。热分解温度大于350℃。连续耐热80-120℃,平衡吸水率2．5％。能耐酸、碱、大多数无机盐水溶液、卤代烷、烃类、酯类、酮类等腐蚀，但易溶于苯酚、甲酸等极性溶剂。具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差。

颗粒：

、

物性表:

Physical Properties	Metric	English	Comments

Density	1.36 g/cc	0.0491 lb/in³	ISO 1183
Water Absorption	6.2 %	6.2 %	ISO 62
Moisture Absorption at Equilibrium	2.4 %	2.4 %	23°C/50% R.H.; ISO 62
Viscosity Test	150 cm³/g	150 cm³/g	Viscosity number
Linear Mold Shrinkage	0.0090 cm/cm	0.0090 in/in	ASTM Data; MD

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	76.0 MPa	11000 psi	0.2 in/min; ASTM Test
Tensile Strength, Ultimate	85.0 MPa	12300 psi	5mm/min; ISO 527
Elongation at Break	5.0 %	5.0 %	0.2 in/min; ASTM Test
	15 %	15 %	5mm/min; ISO 527
Tensile Modulus	4.60 GPa	667 ksi	1mm/min; ISO 527
	5.17 GPa	750 ksi	ASTM Test
Flexural Modulus	4.00 GPa	580 ksi	ISO Data
	4.10 GPa	595 ksi	ASTM Test
Izod Impact, Notched	0.450 J/cm @Temperature -40.0 °C	0.843 ft-lb/in @Temperature -40.0 °F	ASTM Test
	0.640 J/cm @Thickness 3.17 mm	1.20 ft-lb/in @Thickness 0.125 in	ASTM Test
Izod Impact, Notched (ISO)	6.50 kJ/m²	3.09 ft-lb/in²	ISO Test
Charpy Impact Unnotched	22.0 J/cm²	105 ft-lb/in²	ISO 179
	14.5 J/cm² @Temperature -30.0 °C	69.0 ft-lb/in² @Temperature -22.0 °F	ISO 179
Charpy Impact, Notched	0.800 J/cm²	3.81 ft-lb/in²	ISO 179
	0.700 J/cm² @Temperature -30.0 °C	3.33 ft-lb/in² @Temperature -22.0 °F	ISO 179

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+15 ohm-cm	1.00e+15 ohm-cm	IEC 60093
Surface Resistance	1.00e+12 ohm	1.00e+12 ohm	IEC 60093
Dielectric Constant	3.5 @Frequency 1.00e+6 Hz	3.5 @Frequency 1.00e+6 Hz	IEC 60250
Dissipation Factor	0.020 @Frequency 1.00e+6 Hz	0.020 @Frequency 1.00e+6 Hz	IEC 60250
	0.020 @Frequency 100 Hz	0.020 @Frequency 100 Hz	IEC 60250
Comparative Tracking Index	450 V	450 V	IEC 60112

Thermal Properties	Metric	English	Comments
CTE, linear	30.0 µm/m-°C @Temperature -30.0 - 30.0 °C	16.7 µin/in-°F @Temperature -22.0 - 86.0 °F	ASTM Test
CTE, linear, Parallel to Flow	65.0 µm/m-°C	36.1 µin/in-°F	ISO 11359
CTE, linear, Transverse to Flow	60.0 µm/m-°C	33.3 µin/in-°F	ISO 11359
Melting Point	220 °C	428 °F	10 K/min
	220 °C	428 °F	ASTM Test
Deflection Temperature at 0.46 MPa (66 psi)	195 °C	383 °F	ASTM Test
	195 °C	383 °F	ISO 75
Deflection Temperature at 1.8 MPa (264 psi)	120 °C	248 °F	ASTM Test
	120 °C	248 °F	ISO 75
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	HB @Thickness 3.20 mm	HB @Thickness 0.126 in

Descriptive Properties
Color	Natural
Commercial Status	Active America
Form	Pellets
Impact Modified	No
Primary Processing Technique	Injection Molding
Processing	Injection Molding
Special characteristic	Heat stabilized or stable to heat

广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。

上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。

PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。

欢迎各位客户前来咨询：