LCP 7244 材料说明：泽尼特7244®BK010是40%玻璃/矿物增强液晶聚合物树脂与295°C热变形温度高，高流动性和良好的平整度。
LCP 7244 特性：良好的流动性
LCP 7244 加工方法：注塑成型
LCP 7244 的物性表：
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.73 g/cc | 0.0625 lb/in³ | ISO 1183 | ||
| Filler Content | 40 % | 40 % | |||
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm @Thickness 2.00 mm |
0.0010 in/in @Thickness 0.0787 in |
ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm @Thickness 2.00 mm |
0.0050 in/in @Thickness 0.0787 in |
ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 115 MPa | 16700 psi | ISO 527 | ||
| Elongation at Break | 1.4 % | 1.4 % | ISO 527 | ||
| Tensile Modulus | 14.0 GPa | 2030 ksi | ISO 527 | ||
| Flexural Strength | 180 MPa @Temperature 23.0 °C |
26100 psi @Temperature 73.4 °F |
ISO 178 | ||
| Flexural Modulus | 11.3 GPa @Temperature 23.0 °C |
1640 ksi @Temperature 73.4 °F |
ISO 178 | ||
| Charpy Impact, Notched | 0.900 J/cm² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 3.9 @Thickness 2.00 mm, Frequency 1.00e+10 Hz |
3.9 @Thickness 0.0787 in, Frequency 1.00e+10 Hz |
Transverse; ASTM D2520 B | ||
| 4.1 @Thickness 2.00 mm, Frequency 1.00e+9 Hz |
4.1 @Thickness 0.0787 in, Frequency 1.00e+9 Hz |
ASTM D2520 B | |||
| 4.2 @Thickness 2.00 mm, Frequency 1.00e+10 Hz |
4.2 @Thickness 0.0787 in, Frequency 1.00e+10 Hz |
ASTM D2520 B | |||
| 4.2 @Thickness 2.00 mm, Frequency 2.00e+10 Hz |
4.2 @Thickness 0.0787 in, Frequency 2.00e+10 Hz |
ASTM D2520 B | |||
| Dissipation Factor | 0.0040 @Thickness 2.00 mm, Frequency 1.00e+9 Hz |
0.0040 @Thickness 0.0787 in, Frequency 1.00e+9 Hz |
ASTM D2520 B | ||
| 0.0040 @Thickness 2.00 mm, Frequency 1.00e+10 Hz |
0.0040 @Thickness 0.0787 in, Frequency 1.00e+10 Hz |
Transverse; ASTM D2520 B | |||
| 0.0040 @Thickness 2.00 mm, Frequency 1.00e+10 Hz |
0.0040 @Thickness 0.0787 in, Frequency 1.00e+10 Hz |
ASTM D2520 B | |||
| 0.0040 @Thickness 2.00 mm, Frequency 2.00e+10 Hz |
0.0040 @Thickness 0.0787 in, Frequency 2.00e+10 Hz |
ASTM D2520 B | |||
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 3.00 µm/m-°C @Thickness 2.00 mm, Temperature 160 - 260 °C |
1.67 µin/in-°F @Thickness 0.0787 in, Temperature 320 - 500 °F |
ISO 11359-1/-2 | ||
| 4.00 µm/m-°C @Thickness 4.00 mm, Temperature 160 - 260 °C |
2.22 µin/in-°F @Thickness 0.157 in, Temperature 320 - 500 °F |
ISO 11359-1/-2 | |||
| 5.00 µm/m-°C @Thickness 4.00 mm, Temperature -40.0 - 23.0 °C |
2.78 µin/in-°F @Thickness 0.157 in, Temperature -40.0 - 73.4 °F |
ISO 11359-1/-2 | |||
| 5.00 µm/m-°C @Thickness 2.00 mm, Temperature -40.0 - 23.0 °C |
2.78 µin/in-°F @Thickness 0.0787 in, Temperature -40.0 - 73.4 °F |
ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 32.0 µm/m-°C @Temperature -40.0 - 23.0 °C |
17.8 µin/in-°F @Temperature -40.0 - 73.4 °F |
ISO 11359-1/-2; 2mm | ||
| 38.0 µm/m-°C @Temperature -40.0 - 23.0 °C |
21.1 µin/in-°F @Temperature -40.0 - 73.4 °F |
ISO 11359-1/-2; 4mm | |||
| 42.0 µm/m-°C @Temperature -40.0 - 260 °C |
23.3 µin/in-°F @Temperature -40.0 - 500 °F |
ISO 11359-1/-2; 2mm | |||
| 50.0 µm/m-°C @Temperature -40.0 - 260 °C |
27.8 µin/in-°F @Temperature -40.0 - 500 °F |
ISO 11359-1/-2; 4mm | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 295 °C | 563 °F | ISO 75-1/-2 1993/N2 | ||
| UL RTI, Electrical | 130 °C @Thickness 0.750 mm |
266 °F @Thickness 0.0295 in |
UL 746B | ||
| UL RTI, Mechanical with Impact | 130 °C @Thickness 0.750 mm |
266 °F @Thickness 0.0295 in |
UL 746B | ||
| UL RTI, Mechanical without Impact | 130 °C @Thickness 0.750 mm |
266 °F @Thickness 0.0295 in |
UL 746B | ||
| Flammability, UL94 | V-0 @Thickness 0.350 mm |
V-0 @Thickness 0.0138 in |
IEC 60695-11-10 | ||
| V-0 @Thickness 0.350 mm |
V-0 @Thickness 0.0138 in |
UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 365 °C | 689 °F | Optimum | ||
| 360 - 370 °C | 680 - 698 °F | ||||
| Mold Temperature | 80.0 °C | 176 °F | Optimum | ||
| 40.0 - 150 °C | 104 - 302 °F | ||||
| Drying Temperature | 150 °C | 302 °F | |||
| Dry Time | 3 hour | 3 hour | Dehumidified Dryer | ||
| Moisture Content | <= 0.010 % | <= 0.010 % | |||
| De |
|||||
| Color | Black | ||||
| Drying Recommended | Yes | ||||
| Filler | Glass/Mineral | ||||
| Forms | Pellets | ||||
| Generic | LCP | ||||
| Part Marking Code | >LCP-(GF+MD)40< | ISO 11469 | |||
| Polymer Family | LCP | ||||
| Polymer Type | LCP | ||||
| Processing Method | Injection Molding | ||||
| Product Category | Electrical Resins | ||||
| Flame Retardant Resins | |||||
| Glass/Mineral Reinforced Resins | |||||
| Low Warp Resins | |||||
| Region Available | Americas | ||||
| Asia/Pacific | |||||
| Europe | |||||
| Resin Identification | LCP-(GF+MD)40 | ISO 1043 |
|||