主要用途：greenflex FF 35适用于具有良好的断裂力学性能的软包装薄膜，拉伸罩包装型材挤压。
物性表：| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.929 g/cc | 0.929 g/cc | ISO 1183 |
| Vinyl Acetate Content | 9.0 % | 9.0 % | Internal Method |
| Thickness | 30.0 - 150 microns | 1.18 - 5.91 mil | Recommended |
| Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.70 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 94 | 94 | ISO 868/A |
| Hardness, Shore D | 42 | 42 | ISO 868/A |
| Film Tensile Strength at Yield, MD | 7.00 MPa | 1020 psi | ISO 527-3 |
| Film Tensile Strength at Yield, TD | 6.00 MPa | 870 psi | ISO 527-3 |
| Film Elongation at Break, MD | 480 % | 480 % | ISO 527-3 |
| Film Elongation at Break, TD | 650 % | 650 % | ISO 527-3 |
| Coefficient of Friction, Dynamic | >= 0.50 | >= 0.50 | ISO 8295 |
| Elmendorf Tear Strength, MD | 2.038 g/micron | 51.77 g/mil | ISO 6383-2 |
| Elmendorf Tear Strength, TD | 4.076 g/micron | 103.5 g/mil | ISO 6383-2 |
| Dart dro Test | 550 g | 1.21 lb | F50; ISO 7765-1 |
| Film Tensile Strength at Break, MD | 27.0 MPa | 3920 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 28.0 MPa | 4060 psi | ISO 527-3 |
| 1% Secant Modulus, MD | 95.0 MPa | 13800 psi | ISO 527-3 |
| 1% Secant Modulus, TD | 97.0 MPa | 14100 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 102 °C | 216 °F | Internal Method |
| Vicat Softening Point | 75.0 °C @Load 1.00 kg |
167 °F @Load 2.20 lb |
ISO 306/A |
| Brittleness Temperature | <= -80.0 °C | <= -112 °F | ASTM D746 |
| Optical Properties | Metric | English | Comments |
| Haze | 3.0 % | 3.0 % | ISO 14782 |
| Gloss | 75 % | 75 % | 45°; ASTM D2457 |
图：
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com