聚合物；热塑性；液晶聚合物（LCP）；液晶聚合物（LCP），30%的玻璃纤维填充
LCP A130 材料说明：
行业标准。优良的平衡性能，包括易流动，易加工，热稳定性，耐化学性，机械性能和电气性能。适用于气相表面贴装电气和电子设备。30%玻璃增强
LCP A130 的物性表：
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.62 g/cc | 0.0585 lb/in³ | ISO 1183 | ||
| Moisture Absorption | 0.0400 % | 0.0400 % | 23°C/50%RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.00200 cm/cm | 0.00200 in/in | ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.00400 cm/cm | 0.00400 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 85.0 | 85.0 | ISO 2039-2 | ||
| Tensile Strength at Break | 190 MPa | 27600 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 2.10 % | 2.10 % | 5mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 15.0 GPa | 2180 ksi | 50mm/min; ISO 527-2/1A | ||
| Flexural Strength | 280 MPa | 40600 psi | ISO 178 | ||
| Flexural Modulus | 14.5 GPa | 2100 ksi | ISO 178 | ||
| Compressive Strength | 100 MPa @Strain 1.00 % |
14500 psi @Strain 1.00 % |
ISO 604 | ||
| Compressive Modulus | 14.5 GPa | 2100 ksi | ISO 604 | ||
| Izod Impact, Notched (ISO) | 24.0 kJ/m² | 11.4 ft-lb/in² | ISO 180/1A | ||
| 29.0 kJ/m² @Temperature 23.0 °C |
13.8 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |||
| Charpy Impact Unnotched | 3.30 J/cm² | 15.7 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 2.60 J/cm² | 12.4 ft-lb/in² | ISO 179/1eA | ||
| Tensile Creep Modulus, 1 hour | 12600 MPa | 1.83e+6 psi | ISO 899-1 | ||
| Tensile Creep Modulus, 1000 hours | 10900 MPa | 1.58e+6 psi | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.70 @Frequency 1.00e+6 Hz |
3.70 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| 4.20 @Frequency 100 Hz |
4.20 @Frequency 100 Hz |
IEC 60250 | |||
| Dielectric Strength | 31.0 kV/mm | 787 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0160 @Frequency 100 Hz |
0.0160 @Frequency 100 Hz |
IEC 60250 | ||
| 0.0180 @Frequency 1.00e+6 Hz |
0.0180 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Arc Resistance | 140 sec | 140 sec | Internal | ||
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 6.00 µm/m-°C | 3.33 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 23.0 µm/m-°C | 12.8 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 280 °C | 536 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 8.0 MPa | 190 °C | 374 °F | ISO 75-1, -2 | ||
| Vicat Softening Point | 160 °C | 320 °F | ISO 306 | ||
| Flammability, UL94 | V-0 | V-0 | |||
| Oxygen Index | 45.0 % | 45.0 % | ISO 4589 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 - 120 °C | 176 - 248 °F | cavity | ||
| 285 - 295 °C | 545 - 563 °F | hot runner | |||
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| Middle Barrel Temperature | 20.0 - 30.0 °C | 68.0 - 86.0 °F | |||
| Zone 1 | 270 - 280 °C | 518 - 536 °F | |||
| Zone 2 | 275 - 285 °C | 527 - 545 °F | |||
| Zone 3 | 280 - 290 °C | 536 - 554 °F | |||
| Zone 4 | 285 - 295 °C | 545 - 563 °F | |||
| Die Temperature | 290 - 300 °C | 554 - 572 °F | |||
| Melt Temperature | 285 - 295 °C | 545 - 563 °F | |||
| 293 °C | 559 °F | ISO 294 | |||
| Mold Temperature | 60.0 °C | 140 °F | ISO 294 | ||
| Injection Velocity | 150 mm/sec | 5.91 in/sec | ISO 294 | ||
| Drying Temperature | >= 150 °C | >= 302 °F | |||
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |||
| Moisture Content | <= 0.0100 % | <= 0.0100 % | |||
| Injection Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |||
| Hold Pressure | 48.0 MPa | 6960 psi | ISO 294 | ||
| 50.0 - 150 MPa | 7250 - 21800 psi | ||||
| Back Pressure | <= 3.00 MPa | <= 435 psi | |||
| Screw Speed | 80.0 rpm @Diameter 40.0 mm |
80.0 rpm @Diameter 1.57 in |
|||
| 140 rpm @Diameter 25.0 mm |
140 rpm @Diameter 0.984 in |
||||
| 200 rpm @Diameter 16.0 mm |
200 rpm @Diameter 0.630 in |
||||
| De |
|||||
| Injection molding | Yes | ||||
| Injection speed | very fast | ||||