| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.73 g/cc | 0.0625 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | DIN 53495/1L | ||
| Moisture Absorption at Equilibrium | 0.12 % | 0.12 % | 23°C/50% R.H. | ||
| Viscosity Test | 90 cm³/g | 90 cm³/g | Viscosity number | ||
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | Sheet | ||
| 0.0024 cm/cm | 0.0024 in/in | 60x60x2mm; ISO 294 | |||
| Linear Mold Shrinkage, Transverse | 0.0075 cm/cm | 0.0075 in/in | Sheet | ||
| 0.0077 cm/cm | 0.0077 in/in | 60x60x2mm; ISO 294 | |||
| Melt Flow | 10.4 g/10 min @Load 2.16 kg, Temperature 275 °C |
10.4 g/10 min @Load 4.76 lb, Temperature 527 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 165 MPa | 23900 psi | 5mm/min; ISO 527-2 | ||
| Elongation at Break | 1.5 % | 1.5 % | 5mm/min; ISO 527-2 | ||
| Modulus of Elasticity | 18.7 GPa | 2710 ksi | ISO 527-2 | ||
| Charpy Impact Unnotched | 5.20 J/cm² | 24.7 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179/1eA | ||
| Dart Drop, Total Energy | <= 5.00 J | <= 3.69 ft-lb | ISO 6603-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+16 ohm | >= 1.00e+16 ohm | IEC 60093 | ||
Dielectric Constant  |
4.5 @Frequency 1.00e+6 Hz |
4.5 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| 4.7 @Frequency 100 Hz |
4.7 @Frequency 100 Hz |
IEC 60250 | |||
| Dielectric Strength | 16.0 kV/mm | 406 kV/in | IEC 243/1 | ||
| Dissipation Factor |
0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| 0.020 @Frequency 100 Hz |
0.020 @Frequency 100 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 225 V | 225 V | Test solution A; IEC 112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 2.00 - 3.00 µm/m-°C @Temperature 23.0 - 80.0 °C |
1.11 - 1.67 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 53752 | ||
| Specific Heat Capacity | 1.60 J/g-°C | 0.382 BTU/lb-°F | IEC 1006 | ||
| Melting Point | 220 - 250 °C | 428 - 482 °F | |||
| Maximum Service Temperature, Air | 140 °C | 284 °F | at 50% loss of tensile strength after 20000h; IEC 216-1 | ||
| 160 °C | 320 °F | at 50% loss of tensile strength after 5000h; IEC 216-1 | |||
| 210 °C | 410 °F | ||||
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-2 | ||
| Flammability, UL94 |
HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|||
| HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 275 °C | 482 - 527 °F | Injection molding | ||
| 270 °C | 518 °F | for shrinkage test | |||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |||
| 80.0 °C | 176 °F | for shrinkage test | |||
| De |
|||||
| Color | BK5110 and Colored | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Release agent | ||||
图：
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
主要销售：PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。如您需要提前了解原料产品的相关性能或是需要原料产品的相关报告，请您通过电话或是QQ与我联系！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com