LCP MT1300 材料说明：无筋威达级适用于挤压。
LCP MT1300 加工方法：注塑成型
LCP MT1300 的物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0300 % | 0.0300 % | 23°C/50%RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.000 cm/cm | 0.000 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00700 cm/cm | 0.00700 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 182 MPa | 26400 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 3.40 % | 3.40 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 10.6 GPa | 1540 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 158 MPa | 22900 psi | ISO 178 |
| Flexural Modulus | 9.10 GPa | 1320 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 95.0 kJ/m² | 45.2 ft-lb/in² | ISO 180/1A |
| 252 kJ/m² @Temperature 23.0 °C |
120 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 26.7 J/cm² | 127 ft-lb/in² | ISO 179/1eU |
| 5.30 J/cm² @Temperature -30.0 °C |
25.2 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 9.50 J/cm² | 45.2 ft-lb/in² | ISO 179/1eA |
| Tensile Creep Modulus, 1 hour | 9000 MPa | 1.31e+6 psi | ISO 899-1 |
| Tensile Creep Modulus, 1000 hours | 6600 MPa | 957000 psi | ISO 899-1 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 3.00 @Frequency 1.00e+6 Hz |
3.00 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.20 @Frequency 100 Hz |
3.20 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 47.0 kV/mm | 1190 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0159 @Frequency 100 Hz |
0.0159 @Frequency 100 Hz |
IEC 60250 |
| 0.0200 @Frequency 1.00e+6 Hz |
0.0200 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 150 V | 150 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 4.00 µm/m-°C | 2.22 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 38.0 µm/m-°C | 21.1 µin/in-°F | ISO 11359-2 |
| Melting Point | 280 °C | 536 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 187 °C | 369 °F | ISO 75-1, -2 |
| Deflection Temperature at 8.0 MPa | 94.0 °C | 201 °F | ISO 75-1, -2 |
| Vicat Softening Point | 145 °C | 293 °F | ISO 306 |
| Flammability, UL94 | V-0 | V-0 | |