LCP T.rex541 材料说明：挤出成型
LCP T.rex541 的物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.74 g/cc | 0.0629 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 3.00 MPa | 435 psi | 5mm/min; ISO 527-2/1A |
| 110 MPa | 16000 psi | 50mm/min; ISO 527-2/1A | |
| Tensile Modulus | 10.7 GPa | 1550 ksi | 50mm/min; ISO 527-2/1A |
| Flexural Strength | 130 MPa | 18900 psi | ISO 178 |
| Flexural Modulus | 11.7 GPa | 1700 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 2.53 J/cm² | 12.0 ft-lb/in² | ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 357 °C | 675 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO 75-1, -2 |
| Processing Properties | Metric | English | Comments |
| Drying Temperature | >= 150 °C | >= 302 °F | |
| Dry Time | 6.00 hour | 6.00 hour | |
| Moisture Content | <= 0.0100 % | <= 0.0100 % | |