  4. 杜邦高性能聚合物S600F40 NC010低粘度

杜邦高性能聚合物S600F40 NC010低粘度

杜邦高性能聚合物Crastin®S600F40 NC010聚对苯二甲酸丁二醇酯（PBT） 类别：聚合物；热塑性；聚酯，TP；聚对苯二甲酸丁二醇酯（PBT） 材料说明：无筋低粘度聚对苯二甲酸乙二醇酯 Crastin S600F40 NC010是一种无筋润滑的低粘度聚对苯二甲酸乙二醇酯树脂注塑成型。
 物性表：

 
Physical Properties Metric English Comments
Density  1.11 g/cc 0.0401 lb/in³  
  1.31 g/cc 0.0473 lb/in³ ISO 1183
Water Absorption  0.40 %
@Thickness 2.00 mm		 0.40 %
@Thickness 0.0787 in		 Sim. to ISO 62
Moisture Absorption  0.200 %
@Thickness 2.00 mm		 0.200 %
@Thickness 0.0787 in		 Sim. to ISO 62
Viscosity   75900 cP
@Shear Rate 5000 1/s,
Temperature 260 °C		 75900 cP
@Shear Rate 5000 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  86676 cP
@Shear Rate 5000 1/s,
Temperature 250 °C		 86676 cP
@Shear Rate 5000 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  99080 cP
@Shear Rate 5000 1/s,
Temperature 240 °C		 99080 cP
@Shear Rate 5000 1/s,
Temperature 464 °F		 ISO 11403-1 -2
  184900 cP
@Shear Rate 500 1/s,
Temperature 260 °C		 184900 cP
@Shear Rate 500 1/s,
Temperature 500 °F		 ISO 11403-1 -2
  235700 cP
@Shear Rate 500 1/s,
Temperature 250 °C		 235700 cP
@Shear Rate 500 1/s,
Temperature 482 °F		 ISO 11403-1 -2
  301100 cP
@Shear Rate 500 1/s,
Temperature 240 °C		 301100 cP
@Shear Rate 500 1/s,
Temperature 464 °F		 ISO 11403-1 -2
Viscosity Test  120 cm³/g 120 cm³/g ISO 307 1157 1628
Linear Mold Shrinkage, Flow  0.019 cm/cm 0.019 in/in ISO 294-4 2577
Linear Mold Shrinkage, Transverse  0.018 cm/cm 0.018 in/in ISO 294-4 2577
Melt Flow  32.9 g/10 min
@Load 2.16 kg,
Temperature 250 °C		 32.9 g/10 min
@Load 4.76 lb,
Temperature 482 °F		 ISO 1133
 
Mechanical Properties Metric English Comments
Tensile Stress   29.24 MPa
@Strain 1.10 %,
Temperature 23.0 °C		 4241 psi
@Strain 1.10 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  36.41 MPa
@Strain 1.40 %,
Temperature 23.0 °C		 5281 psi
@Strain 1.40 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  41.88 MPa
@Strain 1.40 %,
Temperature -40.0 °C		 6074 psi
@Strain 1.40 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  46.12 MPa
@Strain 1.90 %,
Temperature 23.0 °C		 6689 psi
@Strain 1.90 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  49.47 MPa
@Strain 1.70 %,
Temperature -40.0 °C		 7175 psi
@Strain 1.70 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  50.61 MPa
@Strain 2.20 %,
Temperature 23.0 °C		 7341 psi
@Strain 2.20 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  64.81 MPa
@Strain 2.40 %,
Temperature -40.0 °C		 9400 psi
@Strain 2.40 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  79.66 MPa
@Strain 3.30 %,
Temperature -40.0 °C		 11550 psi
@Strain 3.30 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Tensile Strength, Yield  58.0 MPa 8410 psi ISO 527-1/-2
Elongation at Break  30 % 30 % Nominal; ISO 527-1/-2
Elongation at Yield  6.0 % 6.0 % ISO 527-1/-2
Tensile Modulus  2.60 GPa 377 ksi ISO 527-1/-2
Flexural Strength  85.0 MPa 12300 psi ISO 178
Flexural Modulus  2.40 GPa 348 ksi ISO 178
Secant Modulus   0.371 GPa
@Strain 2.70 %,
Temperature 100 °C		 53.9 ksi
@Strain 2.70 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.426 GPa
@Strain 2.70 %,
Temperature 80.0 °C		 61.8 ksi
@Strain 2.70 %,
Temperature 176 °F		 ISO 11403-1 -2
  0.43735 GPa
@Strain 1.00 %,
Temperature 100 °C		 63.433 ksi
@Strain 1.00 %,
Temperature 212 °F		 ISO 11403-1 -2
  0.4985 GPa
@Strain 1.00 %,
Temperature 80.0 °C		 72.30 ksi
@Strain 1.00 %,
Temperature 176 °F		 ISO 11403-1 -2
  2.05 GPa
@Strain 4.40 %,
Temperature -40.0 °C		 297 ksi
@Strain 4.40 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  2.18 GPa
@Strain 2.40 %,
Temperature 23.0 °C		 317 ksi
@Strain 2.40 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  2.39 GPa
@Strain 2.00 %,
Temperature 23.0 °C		 346 ksi
@Strain 2.00 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  2.60 GPa
@Strain 1.40 %,
Temperature 23.0 °C		 377 ksi
@Strain 1.40 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  2.61 GPa
@Strain 2.70 %,
Temperature -40.0 °C		 378 ksi
@Strain 2.70 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  2.66 GPa
@Strain 1.10 %,
Temperature 23.0 °C		 386 ksi
@Strain 1.10 %,
Temperature 73.4 °F		 ISO 11403-1 -2
  2.91 GPa
@Strain 1.70 %,
Temperature -40.0 °C		 422 ksi
@Strain 1.70 %,
Temperature -40.0 °F		 ISO 11403-1 -2
  2.99 GPa
@Strain 1.40 %,
Temperature -40.0 °C		 434 ksi
@Strain 1.40 %,
Temperature -40.0 °F		 ISO 11403-1 -2
Izod Impact, Notched (ISO)  4.00 kJ/m² 1.90 ft-lb/in² ISO 180/1A
Charpy Impact Unnotched  NB NB ISO 179/1eU
  NB
@Temperature -30.0 °C		 NB
@Temperature -22.0 °F		 ISO 179/1eU
Charpy Impact, Notched  0.400 J/cm² 1.90 ft-lb/in² ISO 179/1eA
  0.400 J/cm²
@Temperature -30.0 °C		 1.90 ft-lb/in²
@Temperature -22.0 °F		 ISO 179/1eA
Tensile Creep Modulus, 1 hour  2600 MPa
@Time 3600 sec		 377000 psi
@Time 1.00 hour		 ISO 899-1
Tensile Creep Modulus, 1000 hours  1800 MPa
@Time 3.60e+6 sec		 261000 psi
@Time 1000 hour		 ISO 899-1
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+15 ohm-cm >= 1.00e+15 ohm-cm IEC 60093
Dielectric Constant   3.2
@Frequency 1.00e+6 Hz		 3.2
@Frequency 1.00e+6 Hz		 IEC 60250
  3.8
@Frequency 100 Hz		 3.8
@Frequency 100 Hz		 IEC 60250
Dielectric Strength  26.0 kV/mm 660 kV/in IEC 60243-1
Dissipation Factor   0.0020
@Frequency 100 Hz		 0.0020
@Frequency 100 Hz		 IEC 60250
  0.020
@Frequency 1.00e+6 Hz		 0.020
@Frequency 1.00e+6 Hz		 IEC 60250
Comparative Tracking Index  600 V 600 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  110 µm/m-°C 61.1 µin/in-°F ISO 11359-1/-2
CTE, linear, Transverse to Flow  120 µm/m-°C 66.7 µin/in-°F ISO 11359-1/-2
Specific Heat Capacity  2.11 J/g-°C 0.504 BTU/lb-°F  
Thermal Conductivity  0.210 W/m-K 1.46 BTU-in/hr-ft²-°F of melt
Melting Point  225 °C 437 °F 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)  115 °C 239 °F ISO 75-1/-2
  180 °C 356 °F annealed; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)  50.0 °C 122 °F ISO 75-1/-2
  60.0 °C 140 °F annealed; ISO 75-1/-2
Vicat Softening Point  175 °C 347 °F 50°C/h 50N; ISO 306
Glass Transition Temp, Tg  55.0 °C 131 °F 10°C/min; ISO 11357-1/-2
Flammability, UL94   HB
@Thickness 1.50 mm		 HB
@Thickness 0.0591 in		 IEC 60695-11-10
  HB
@Thickness 0.800 mm		 HB
@Thickness 0.0315 in		 IEC 60695-11-10
Oxygen Index  22 % 22 % ISO 4589-1/-2
 
Descriptive Properties
Additives Release agent  
Delivery form Pellets  
Part Marking Code >PBT< ISO 11469
Processing Injection Moulding  
Regional Availability Asia Pacific  
  Europe  
  Global  
  Near East/Africa  
  North America  
  South and Central America  
Resin Identification PBT  
UL recognition UL


图：

 
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！
我司所销售所有产品均为原厂原包，均可提供相关资料报告（如：物性表，MSDS报告，UL报告，COA报告，SGS报告，FDA等）！
欢迎新老客户来电或QQ咨询：
联系人：李先生
联系电话；13636696005
联系QQ；1020580970
联系邮箱；1020580970@qq.com

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-40888.html

免责声明: 本文 杜邦高性能聚合物S600F40 NC010低粘度 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他资讯信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4