LCP A515 材料说明：
LCP A515 性能表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | ISO 1183 |
| Water Absorption | 0.020 % | 0.020 % | Immersion to equilibrium; ISO 62 |
| Moisture Absorption at Equilibrium | 0.020 % | 0.020 % | ISO 62 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm | 0.0040 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 63 | 63 | ISO 2039-2 |
| Tensile Strength, Ultimate | 175 MPa | 25400 psi | ISO 527 |
| Elongation at Break | 4.6 % | 4.6 % | IEC 527 |
| Tensile Modulus | 14.0 GPa | 2030 ksi | ISO 527 |
| Flexural Strength | 170 MPa | 24700 psi | ISO 178 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ISO 178 |
| Compressive Strength | 61.0 MPa | 8850 psi | 1% Deflection, ISO 604 |
| Compressive Modulus | 10.0 GPa | 1450 ksi | ISO 604 |
| Izod Impact, Notched (ISO) | 60.0 kJ/m² | 28.6 ft-lb/in² | ISO 180/1A |
| Charpy Impact, Notched | 2.10 J/cm² | 9.99 ft-lb/in² | ISO 179 |
| Tensile Impact Strength | 80.0 kJ/m² | 38.1 ft-lb/in² | Notched; ASTM D1822 |
| Coefficient of Friction, Dynamic | 0.19 | 0.19 | vs. steel; ASTM D1984 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+17 ohm | 1.00e+17 ohm | IEC 93 |
| Dielectric Constant | 3.1 @Frequency 1e+7 Hz |
3.1 @Frequency 1e+7 Hz |
|
| 3.6 @Frequency 1000 Hz |
3.6 @Frequency 1000 Hz |
IEC 250 | |
| Dissipation Factor | 0.0090 @Frequency 1e+7 Hz |
0.0090 @Frequency 1e+7 Hz |
|
| 0.030 @Frequency 1000 Hz |
0.030 @Frequency 1000 Hz |
IEC 250 | |
| Arc Resistance | 145 sec | 145 sec | |
| Comparative Tracking Index | 175 V | 175 V | IEC 112 |