- 熔体流动速率 [g/10min]: 15.0
- 密度 [g/cm3]: 0.936
- 弯曲模量 [MPa]: 62.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.936 g/cc | 0.0338 lb/in³ | ASTM D1505 | ||
| Vinyl Acetate Content | 16 % | 16 % | |||
| Melt Flow | 15 g/10 min | 15 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 41 | 41 | 15s; ASTM D2240 | ||
| Tensile Strength at Break | 10.7 MPa | 1550 psi | ASTM D638 | ||
| Elongation at Break | 590 % | 590 % | ASTM D638 | ||
| Flexural Modulus, 1% Secant | 62.1 MPa | 9000 psi | ASTM D790 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 79.0 °C | 174 °F | Peak; Westlake Method | ||
| Vicat Softening Point | 65.0 °C | 149 °F | ASTM D1525 | ||
| Descriptive Properties | |||||
| Process | Coating | ||||
| Film | |||||
| Region | US & Canada | ||||