- 密度 [g/cm3]: 0.941
- 弯曲强度 [MPa]: 15.0
- 弯曲模量 [MPa]: 0.0400
- 脆化温度 [℃]: -100.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.941 g/cc | 0.0340 lb/in³ | ASTM D792 | ||
| Vinyl Acetate Content | 18 % | 18 % | TGA | ||
| Melt Index of Compound | 8.0 g/10 min | 8.0 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 88 | 88 | ASTM D2240 | ||
| Hardness, Shore D | 38 | 38 | ASTM D2240 | ||
| Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | Type IV, crosshead speed 2 in/min; ASTM D638 | ||
| 5.50 MPa @Temperature 49.0 °C | 798 psi @Temperature 120 °F | Type IV, crosshead speed 2 in/min; ASTM D638 | |||
| 28.0 MPa @Temperature -20.0 °C | 4060 psi @Temperature -4.00 °F | Type IV, crosshead speed 2 in/min, at -20°C; ASTM D638 | |||
| Elongation at Break | 800 % | 800 % | Type IV, crosshead speed 2 in/min; ASTM D638 | ||
| 450 % @Temperature -20.0 °C | 450 % @Temperature -4.00 °F | Type IV, crosshead speed 2 in/min, at -20°C; ASTM D638 | |||
| 750 % @Temperature 49.0 °C | 750 % @Temperature 120 °F | Type IV, crosshead speed 2 in/min; ASTM D638 | |||
| Modulus of Elasticity | 0.0370 GPa | 5.37 ksi | |||
| 0.159 GPa @Temperature -20.0 °C | 23.1 ksi @Temperature -4.00 °F | ||||
| Flexural Modulus | 0.0400 GPa | 5.80 ksi | ASTM D790 | ||
| 0.0180 GPa @Temperature 49.0 °C | 2.61 ksi @Temperature 120 °F | ASTM D790 | |||
| 0.197 GPa @Temperature -20.0 °C | 28.6 ksi @Temperature -4.00 °F | ASTM D790 | |||
| Flexural Stiffness | 37.0006 MPa | 5366.48 psi | |||
| 159.0 MPa @Temperature -20.0 °C | 23060 psi @Temperature -4.00 °F | ||||
| Tensile Impact Strength | 455 kJ/m² | 217 ft-lb/in² | At -20°C; ASTM D1822 | ||
| 525 kJ/m² | 250 ft-lb/in² | At 23°C; ASTM D1822 | |||
| Compression Set | 49 % | 49 % | Method B, 10 days at 25°C; ASTM D395 | ||
| 90 % @Temperature 70.0 °C | 90 % @Temperature 158 °F | Method B, 22 hours; ASTM D395 | |||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 61.0 °C | 142 °F | ASTM D1525 | ||
| Brittleness Temperature | <= -100 °C | <= -148 °F | ASTM D762 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 121 - 204 °C | 250 - 399 °F | |||
| Descriptive Properties | |||||
| Cycle time | 0.5-2 minutes | Molding, equipment and part design dependent | |||
| Vinyl Acetate Content | 18 wt.% | ||||