- 熔体流动速率 [g/10min]: 0.9
- 密度 [g/cm3]: 0.93
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | Exxon Method |
| Thickness | 31.8 microns | 1.25 mil | |
| Melt Flow | 0.90 g/10 min | 0.90 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 7.60 MPa | 1100 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 6.20 MPa | 899 psi | ASTM D882 |
| Film Elongation at Break, MD | 230 % | 230 % | ASTM D882 |
| Film Elongation at Break, TD | 635 % | 635 % | ASTM D882 |
| Secant Modulus, MD | 0.130 GPa | 18.9 ksi | ASTM D882 |
| Secant Modulus, TD | 0.160 GPa | 23.2 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 110 g | 110 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 70 g | 70 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 3.46 g/micron | 88.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 2.20 g/micron | 56.0 g/mil | ASTM D1922 |
| Dart Drop | 7.87 g/micron | 200 g/mil | F50; ASTM D1709 |
| Dart drop Test | 250 g | 0.551 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 37.0 MPa | 5370 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 28.0 MPa | 4060 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 99.0 °C | 210 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 3.0 % | 3.0 % | ASTM D1003 |
| Gloss | 77 % | 77 % | 45°, ASTM D-2457 |
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified |