- 密度 [g/cm3]: 1.35
- 缺口冲击强度: 8.0
- 断裂伸长率 [%]: 62.0
- 弯曲强度 [MPa]: 45.0
- 弯曲模量 [MPa]: 2.41
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ASTM D638 |
| Elongation at Break | 189 % | 189 % | ASTM D638 |
| Flexural Yield Strength | 62.0 MPa | 8990 psi | ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 |
| Izod Impact, Notched | 8.00 J/cm @Thickness 3.17 mm | 15.0 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.0 °C | 160 °F | annealed; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | V-0, 5V; UL Standard 94 |