- 熔体流动速率 [g/10min]: 5.2
- 密度 [g/cm3]: 1.05
- 吸水率 [%]: 0.1
- 缺口冲击强度: 0.27
- 拉伸强度 [MPa]: 36.0
- 弯曲模量 [MPa]: 2.17
- 硬度: 76.0
- 透光率 [%]: 89.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 5.2 g/10 min @Load 5.00 kg, Temperature 200 °C | 5.2 g/10 min @Load 11.0 lb, Temperature 392 °F | ASTM D1238 |
| Chemical Properties | Metric | English | Comments |
| Styrene Content | <= 0.10 % | <= 0.10 % | Residual Styrene Monomer Content per Berre Laboratory Analytical Methods 0075 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 76 | 76 | ASTM D785 |
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | 0.2 in/min; ASTM D638 |
| Elongation at Break | 40 % | 40 % | 0.2 in/min; ASTM D638 |
| Modulus of Elasticity | 2.28 GPa | 331 ksi | 0.2 in/min; ASTM D638 |
| Flexural Strength | 57.0 MPa | 8270 psi | 0.05 in/min; ASTM D790 |
| Flexural Modulus | 2.17 GPa | 315 ksi | 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 0.270 J/cm | 0.506 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | ASTM D648 |
| Vicat Softening Point | 99.0 °C | 210 °F | ASTM D1525 |
| Flammability, UL94 | HB | HB | 0.060 in for all colors |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.57 | 1.57 | ASTM D542 |
| Haze | 1.6 % | 1.6 % | ASTM D1003 |
| Transmission, Visible | 89.2 % | 89.2 % | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | <= 243 °C | <= 469 °F | |
| Rear Barrel Temperature | 188 - 221 °C | 370 - 430 °F | |
| Middle Barrel Temperature | 193 - 227 °C | 379 - 441 °F | |
| Front Barrel Temperature | 199 - 232 °C | 390 - 450 °F | |
| Melt Temperature | 210 - 243 °C | 410 - 469 °F | |
| Mold Temperature | 27.0 - 54.0 °C | 80.6 - 129 °F | |
| Drying Temperature | 65.6 °C | 150 °F | |
| Dry Time | 2 hour | 2 hour | |