- 密度 [g/cm3]: 1.19
- 吸水率 [%]: 0.4
- 缺口冲击强度: 0.149
- 弯曲模量 [MPa]: 3.38
- 热变形温度 [℃]: 97.2
- 透光率 [%]: 92.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 | ||
| Water Absorption | 0.40 % | 0.40 % | ASTM D570 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 95 | 95 | ASTM D785 | ||
| Tensile Strength | 76.05 MPa | 11030 psi | ASTM D638 | ||
| Elongation at Break | 5.8 % | 5.8 % | ASTM D638 | ||
| Tensile Modulus | 3.38 GPa | 490 ksi | ASTM D638 | ||
| Flexural Strength | 117 MPa | 17000 psi | ASTM D790 | ||
| Flexural Modulus | 3.38 GPa | 490 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.149 J/cm | 0.280 ft-lb/in | Milled Notch; ASTM D256 | ||
| 0.214 J/cm | 0.400 ft-lb/in | Molded Notch; ASTM D256 | |||
| Tensile Impact Strength | 42.0 kJ/m² | 20.0 ft-lb/in² | ASTM D1822 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 54.0 µm/m-°C @Temperature -34.4 - -1.11 °C | 30.0 µin/in-°F @Temperature -30.0 - 30.0 °F | ASTM D696 | ||
| Thermal Conductivity | 0.130 W/m-K | 0.900 BTU-in/hr-ft²-°F | ASTM C177 | ||
| Melting Point | 149 - 157 °C | 300 - 315 °F | |||
| Maximum Service Temperature, Air | 76.7 - 87.8 °C | 170 - 190 °F | Continuous | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 97.2 °C | 207 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ASTM D648 | ||
| Softening Point | 98.9 - 104 °C | 210 - 220 °F | |||
| Flame Spread Index | 115 | 115 | ASTM E84 | ||
| Shrinkage | <= 5.0 % | <= 5.0 % | ASTM D702 | ||
| Optical Properties | Metric | English | Comments | ||
| Refractive Index | 1.49 | 1.49 | ASTM D542 | ||
| Haze | 2.0 % | 2.0 % | ASTM D1003 | ||
| Transmission, Visible | 92 % | 92 % | ASTM D1003 | ||
| Descriptive Properties | |||||
| Flammability | B2 | ||||
| Flammability Burn Rate | 1.019 in/min | ASTM D635 | |||
| Self Ignition Temperature | 833°F | ASTM D1929 | |||
| Smoke Developed Index | 550 | ASTM E84 | |||