- 密度 [g/cm3]: 1.5
- 缺口冲击强度: 2.4
- 拉伸强度 [MPa]: 15.0
- 弯曲模量 [MPa]: 3.20
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 |
| Filler Content | 60 % | 60 % | ISO 3451 / 1 |
| Melt Index of Compound | 20 g/10 min @Load 2.16 kg, Temperature 230 °C | 20 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 75 | 75 | ISO 868 |
| Tensile Strength, Yield | 15.0 MPa | 2180 psi | ISO 527 |
| Elongation at Break | 20 % | 20 % | ISO 527 |
| Elongation at Yield | 3.0 % | 3.0 % | ISO 527 |
| Flexural Modulus | 3.20 GPa | 464 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 2.40 kJ/m² | 1.14 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75 |
| Vicat Softening Point | 110 °C | 230 °F | 49 N; ISO 306 |