- 熔体流动速率 [g/10min]: 12.0
- 密度 [g/cm3]: 1.14
- 拉伸强度 [MPa]: 19.0
- 热变形温度 [℃]: 108.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C | 12 g/10 min @Load 4.76 lb, Temperature 446 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 19.0 MPa | 2760 psi | 50 mm/min |
| Elongation at Break | 7.0 % | 7.0 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 3.0 % | 3.0 % | 50 mm/min |
| Tensile Modulus | 2.70 GPa | 392 ksi | 1 mm/min |
| Charpy Impact Unnotched | 4.60 J/cm² | 21.9 ft-lb/in² | |
| 1.90 J/cm² @Temperature -30.0 °C | 9.04 ft-lb/in² @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 1.10 J/cm² | 5.24 ft-lb/in² | |
| 0.260 J/cm² @Temperature -30.0 °C | 1.24 ft-lb/in² @Temperature -22.0 °F | ||
| Thermal Properties | Metric | English | Comments |
| Melting Point | 163 °C | 325 °F | 10°C/min |
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | |
| Vicat Softening Point | 52.0 °C | 126 °F | 50°C/hr; 50N |