- 熔体流动速率 [g/10min]: 15.0
- 缺口冲击强度: 1.07
- 拉伸强度 [MPa]: 22.8
- 弯曲模量 [MPa]: 1.65
- 硬度: 86.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.00 g/cc | 1.00 g/cc | ASTM D792 |
| Melt Flow | 15 - 20 g/10 min @Temperature 230 °C | 15 - 20 g/10 min @Temperature 446 °F | Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 86 | 86 | ASTM D785 |
| Tensile Strength, Yield | 22.8 MPa | 3300 psi | ASTM D638 |
| Elongation at Break | 25 % | 25 % | ASTM D638 |
| Flexural Modulus | 1.65 GPa | 240 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm | 2.00 ft-lb/in | ASTM D256 |
| NB | NB | ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 103 °C | 217 °F | ASTM D648 |