- 熔体流动速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.9
- 拉伸强度 [MPa]: 18.0
- 弯曲模量 [MPa]: 0.800
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in³ | ISO 1183 |
| Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 230 °C | 0.30 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 59 | 59 | ISO 868 |
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 4.0 % | 4.0 % | At 50 mm/min; ISO 527-2 |
| Flexural Modulus | 0.800 GPa | 116 ksi | At 2 mm/min; ISO 178 |
| Charpy Impact, Notched | 6.50 J/cm² @Temperature -20.0 °C | 30.9 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eA |
| 7.50 J/cm² @Temperature 0.000 °C | 35.7 ft-lb/in² @Temperature 32.0 °F | ISO 179/1eA | |
| Processing Properties | Metric | English | Comments |
| Front Barrel Temperature | 210 - 230 °C | 410 - 446 °F | |
| Die Temperature | 230 - 240 °C | 446 - 464 °F | |
| Melt Temperature | 230 - 240 °C | 446 - 464 °F | |
| Head Temperature | 230 - 240 °C | 446 - 464 °F | |