- 吸水率 [%]: 3.3
- 弯曲强度 [MPa]: 45.68
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Water Absorption | 3.3 % @Time 2.59e+6 sec | 3.3 % @Time 720 hour | immersion; cured 7 days @ 25°C | ||
| 3.3 % @Time 2.59e+6 sec | 3.3 % @Time 720 hour | immersion; cured 30 days @ 25°C | |||
| Viscosity | 2260 cP | 2260 cP | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 33 @Temperature 75.0 °C | 33 @Temperature 167 °F | cured 7 days @ 25°C | ||
| 42 @Temperature 75.0 °C | 42 @Temperature 167 °F | cured 30 days @ 25°C | |||
| 82 @Temperature 25.0 °C | 82 @Temperature 77.0 °F | cured 7 days @ 25°C | |||
| 84 @Temperature 25.0 °C | 84 @Temperature 77.0 °F | cured 30 days @ 25°C | |||
| 86 @Temperature 0.000 °C | 86 @Temperature 32.0 °F | cured 30 days @ 25°C | |||
| 87 @Temperature 0.000 °C | 87 @Temperature 32.0 °F | cured 7 days @ 25°C | |||
| 89 @Temperature -60.0 °C | 89 @Temperature -76.0 °F | cured 7 days @ 25°C | |||
| 89 @Temperature -60.0 °C | 89 @Temperature -76.0 °F | cured 30 days @ 25°C | |||
| Tensile Strength, Ultimate | 45.68 MPa | 6625 psi | cured 7 days @ 25°C | ||
| 48.6 MPa | 7050 psi | cured 30 days @ 25°C | |||
| Elongation at Break | 12 % | 12 % | cured 30 days @ 25°C | ||
| 20 % | 20 % | cured 7 days @ 25°C | |||
| Shear Strength | 2.55 MPa @Temperature 75.0 °C | 370 psi @Temperature 167 °F | Tensile, Al/Al lap joint; cured 7 days @ 25°C | ||
| 27.2 MPa @Temperature 25.0 °C | 3950 psi @Temperature 77.0 °F | Tensile, Al/Al lap joint; cured 7 days @ 25°C | |||
| 30.3 MPa @Temperature 0.000 °C | 4400 psi @Temperature 32.0 °F | Tensile, Al/Al lap joint; cured 7 days @ 25°C | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 4.60e+9 ohm-cm @Temperature 100 °C | 4.60e+9 ohm-cm @Temperature 212 °F | cured 30 days @ 25°C | ||
| 1.70e+10 ohm-cm @Temperature 100 °C | 1.70e+10 ohm-cm @Temperature 212 °F | cured 7 days @ 25°C | |||
| 3.30e+14 ohm-cm @Temperature 25.0 °C | 3.30e+14 ohm-cm @Temperature 77.0 °F | cured 30 days @ 25°C | |||
| 7.10e+14 ohm-cm @Temperature 25.0 °C | 7.10e+14 ohm-cm @Temperature 77.0 °F | cured 7 days @ 25°C | |||
| Processing Properties | Metric | English | Comments | ||
| Pot Life | 40 min @Temperature 25.0 °C | 40 min @Temperature 77.0 °F | 200 g | ||
| Descriptive Properties | |||||
| Parts by Weight (pbw) | 100 | AboCast 8110-2 | |||
| 16.5 | AboCure 8110-2 | ||||