- 吸水率 [%]: 0.17
- 缺口冲击强度: 0.234
- 断裂伸长率 [%]: 110.32
- 弯曲强度 [MPa]: 61.36
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Absorption | 0.17 % | 0.17 % | in 24 hours. |
| Viscosity Measurement | 4000 | 4000 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 86 | 86 | |
| Tensile Strength, Ultimate | 61.36 MPa | 8900 psi | |
| Elongation at Break | 2.5 % | 2.5 % | |
| Modulus of Elasticity | 3.309 GPa | 479.9 ksi | |
| Flexural Yield Strength | 110.32 MPa | 16001 psi | |
| Compressive Yield Strength | 91.01 MPa | 13200 psi | |
| Izod Impact, Notched | 0.234 J/cm | 0.438 ft-lb/in | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 2.00e+11 ohm-cm @Temperature 93.3 °C | 2.00e+11 ohm-cm @Temperature 200 °F | |
| 1.00e+13 ohm-cm @Temperature 65.6 °C | 1.00e+13 ohm-cm @Temperature 150 °F | ||
| 1.00e+15 ohm-cm @Temperature 25.0 °C | 1.00e+15 ohm-cm @Temperature 77.0 °F | ||
| Dielectric Constant | 3.97 @Frequency 1e+6 Hz | 3.97 @Frequency 1e+6 Hz | |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz | 0.020 @Frequency 1e+6 Hz | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 86.0 °C | 187 °F | Deflection temperature; load unknown. |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 25.0 °C | 77.0 °F | Curing time: 2 weeks |