- 吸水率 [%]: 0.19
- 缺口冲击强度: 0.2
- 断裂伸长率 [%]: 78.6
- 弯曲强度 [MPa]: 42.75
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Absorption | 0.19 % | 0.19 % | in 24 hours. |
| Viscosity Measurement | 700 | 700 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 82 | 82 | |
| Tensile Strength, Ultimate | 42.75 MPa | 6200 psi | |
| Elongation at Break | 2.4 % | 2.4 % | |
| Modulus of Elasticity | 3.172 GPa | 460.1 ksi | |
| Flexural Yield Strength | 78.6 MPa | 11400 psi | |
| Compressive Yield Strength | 73.08 MPa | 10600 psi | |
| Izod Impact, Notched | 0.200 J/cm | 0.375 ft-lb/in | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 2.30e+9 ohm-cm @Temperature 93.3 °C | 2.30e+9 ohm-cm @Temperature 200 °F | |
| 1.40e+11 ohm-cm @Temperature 65.6 °C | 1.40e+11 ohm-cm @Temperature 150 °F | ||
| 1.30e+15 ohm-cm @Temperature 25.0 °C | 1.30e+15 ohm-cm @Temperature 77.0 °F | ||
| Dielectric Constant | 3.81 @Frequency 1e+6 Hz | 3.81 @Frequency 1e+6 Hz | |
| Dissipation Factor | 0.010 @Frequency 1e+6 Hz | 0.010 @Frequency 1e+6 Hz | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 82.0 °C | 180 °F | Deflection temperature; load unknown. |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 25.0 °C | 77.0 °F | Curing time: 2 weeks |