- 弯曲强度 [MPa]: 39.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 490000 cP | 490000 cP | Mixed | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 85 | 85 | |||
| Tensile Strength, Ultimate | 39.0 MPa | 5650 psi | after optimum cure | ||
| Elongation at Break | 2.1 % | 2.1 % | |||
| Adhesive Bond Strength | 59.6 MPa | 8650 psi | Steel-Steel; after optimum cure | ||
| 14.5 MPa @Temperature -54.4 °C | 2100 psi @Temperature -66.0 °F | Aluminum-Aluminum tensile shear | |||
| 16.2 MPa @Temperature 82.2 °C | 2350 psi @Temperature 180 °F | Aluminum-Aluminum tensile shear | |||
| 20.3 MPa @Temperature 25.0 °C | 2950 psi @Temperature 77.0 °F | Aluminum-Aluminum tensile shear | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 48.0 µm/m-°C @Temperature 20.0 °C | 26.7 µin/in-°F @Temperature 68.0 °F | |||
| Glass Transition Temp, Tg | 98.0 °C | 208 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 93.3 °C | 200 °F | Optimum cure is 1 hr. @ 200°F | ||
| Pot Life | 120 - 180 min | 120 - 180 min | Max working life at 25°C (100 g) | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| Mix Ratio | 100/6 | By Weight | |||