| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | |||
| Solids Content | 44.2 % | 44.2 % | by weight | ||
| 46.1 % | 46.1 % | by volume | |||
| Volatile Organic Compounds (VOC) Content | 117 g/l | 117 g/l | |||
| Viscosity | 400 - 900 cP | 400 - 900 cP | |||
| Thickness | 38.1 microns | 1.50 mil | recommended dry film thickness | ||
| 102 microns | 4.00 mil | estimated wet film thickness | |||
| Storage Temperature | 4.44 - 32.2 °C | 40.0 - 90.0 °F | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 593 °C | 1100 °F | |||
| Flash Point | >= 100 °C | >= 212 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 10.0 - 48.9 °C | 50.0 - 120 °F | Application Temperature | ||
| Dry Time | 1 hour | 1 hour | Handling | ||
| 2 hour | 2 hour | Touch | |||
| >= 2.5 hour | >= 2.5 hour | Recoat | |||
| Cure Time | 45.0 min | 0.750 hour | at 450°F; Adequate ventilation is required when curing these products. Outgassing will occur above 300°F and cease after 750°F. An additional 30 minutes is required at the highest service temperature if service temperature is below 750°F. | ||
| >= 60.0 min | >= 1.00 hour | Air Set prior to curing | |||
| Shelf Life | 6.00 Month | 6.00 Month | |||
| Descriptive Properties | |||||
| Dry Film Coverage ft2/gal | 740 | at 1 mil | |||
| Thinner | Water | ||||