- 弯曲强度 [MPa]: 4.72
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 2.70 g/cc | 2.70 g/cc | silicone property; Arlon SQA-TMS-024 | ||
| Thickness | 102 microns | 4.00 mil | layer 1; Arlon SQA-TMS-003 | ||
| 305 microns | 12.0 mil | layer 2; Arlon SQA-TMS-003 | |||
| 457 microns | 18.0 mil | substrate; Arlon SQA-TMS-003 | |||
| 864 microns | 34.0 mil | overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 77 | 77 | silicone property; ASTM D2240 | ||
| Tensile Strength, Ultimate | 4.72 MPa | 685 psi | silicone property; ASTM D412 | ||
| Elongation at Break | 125 % | 125 % | silicone property; ASTM D412 | ||
| Adhesive Bond Strength | 0.0155 MPa | 2.25 psi | Arlon SQA-TMS-011 | ||
| Tear Strength | 8.77 kN/m | 50.0 pli | Die B; silicone property; ASTM D624 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 16.7 kV/mm | 425 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Thermal Conductivity | 1.70 W/m-K | 11.8 BTU-in/hr-ft²-°F | overall; Arlon SQA-TMS-054 | ||
| 1.40 W/m-K @Temperature 100 °C | 9.72 BTU-in/hr-ft²-°F @Temperature 212 °F | silicone property; ASTM E1530 | |||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | |||
| 15.0 min @Pressure 0.345 MPa, Temperature 121 °C | 0.250 hour @Pressure 50.0 psi, Temperature 250 °F | ||||
| Shelf Life | 6.00 Month @Temperature 7.22 °C | 6.00 Month @Temperature 45.0 °F | |||
| Descriptive Properties | |||||
| Color | Gray | ||||