- 密度 [g/cm3]: 1.2
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 76.2 microns | 3.00 mil | Interleave | ||
| 203 microns | 8.00 mil | Side 1; Arlon SQA-TMS-003 | |||
| 203 microns | 8.00 mil | Substrate; Arlon SQA-TMS-003 | |||
| 406 microns | 16.0 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 47 | 47 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 6.89 MPa | 1000 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 400 % | 400 % | Silicone Property; ASTM D412 | ||
| Peel Strength | 1.74 kN/m | 9.90 pli | Bond Strength; Arlon SQA-TMS-023 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -73.3 °C | -100 °F | |||
| Flammability Test | 1.3 | 1.3 | [in], Char; FTMS 191A, Method 5903 | ||
| 6.0 | 6.0 | [sec], Flame/Glow; FTMS 191A, Method 5903 | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 8.00 min @Pressure 0.552 MPa, Temperature 138 °C | 0.133 hour @Pressure 80.0 psi, Temperature 280 °F | Bond Cycle | ||
| Shelf Life | 6.00 Month @Temperature 23.9 °C | 6.00 Month @Temperature 75.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Red | ||||
| Total Product Weight (oz/yd2) | 14.6 | Arlon SQA-TMS-025 | |||