- 密度 [g/cm3]: 1.26
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 76.2 microns | 3.00 mil | Interleave | ||
| 102 microns | 4.00 mil | Substrate; Arlon SQA-TMS-003 | |||
| 406 microns | 16.0 mil | Side 1; Arlon SQA-TMS-003 | |||
| 508 microns | 20.0 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 59 | 59 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 7.86 MPa | 1140 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 340 % | 340 % | Silicone Property; ASTM D412 | ||
| Tear Strength | 17.0 kN/m | 97.0 pli | [ppiw], Die B, Silicone Property; ASTM D624 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 34.9 kV/mm | 886 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Flammability, UL94 | HB @Temperature 220 °C | HB @Temperature 428 °F | per card E54153 | ||
| Flammability Test | 0.30 | 0.30 | [in], Char Length; FAR 25.853 App.F, P.1,.Aii | ||
| 10.4 | 10.4 | [sec], Flame and Afterglow; FAR 25.853 App.F, P.1,.Aii | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | ||
| Shelf Life | 60.0 Month @Temperature 21.1 °C | 60.0 Month @Temperature 70.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | White | ||||
| White | Substrate | ||||
| Total Product Weight (oz/yd2) | 19.5 | Arlon SQA-TMS-025 | |||