- 密度 [g/cm3]: 1.35
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | <= 12.7 microns | <= 0.500 mil | Side 1; Arlon SQA-TMS-003 | ||
| 63.5 microns | 2.50 mil | Interleave | |||
| 76.2 microns | 3.00 mil | Side 2; Arlon SQA-TMS-003 | |||
| 203 microns | 8.00 mil | Substrate; Arlon SQA-TMS-003 | |||
| 279 microns | 11.0 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 51 | 51 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 8.07 MPa | 1170 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 560 % | 560 % | Silicone Property; ASTM D412 | ||
| Peel Strength | 1.53 kN/m | 8.70 pli | (S1 to S2), Bond Strength; Arlon SQA-TMS-011 | ||
| 2.23 kN/m | 12.7 pli | (S2 to S2), Bond Strength; Arlon SQA-TMS-011 | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 177 °C | 0.250 hour @Pressure 50.0 psi, Temperature 350 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 23.9 °C | 6.00 Month @Temperature 75.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Red | ||||
| Total Product Weight (oz/yd2) | 11.8 | Arlon SQA-TMS-025 | |||