Arlon 55578R028 0.028" (0.711 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate物性表参数

Arlon 55578R028 0.028" (0.711 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate

Arlon 55578R028 0.028" (0.711 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate 物性表: Arlon 55578R028 0.028" (0.711 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate物性表及特性介绍,Arlon 55578R028 0.028" (0.711 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate注塑参数详情,如需Arlon 55578R028 0.028" (0.711 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate下载, 可到相关下载区下载

密度 [g/cm3]: 1.24

Physical Properties	Metric	English	Comments

Density	1.24 g/cc	0.0448 lb/in³	Side 2, Layer 2; Compound Property; Arlon SQA-TMS-024
	1.35 g/cc	0.0488 lb/in³	Side 1 and Side 2, Layer 1; Compound Property; Arlon SQA-TMS-024
Thickness	38.1 microns	1.50 mil	Side 1; Arlon SQA-TMS-003
	63.5 microns	2.50 mil	Interleave
	76.2 microns	3.00 mil	Side 2, Layer 1; Arlon SQA-TMS-003
	191 microns	7.50 mil	Side 2, Layer 2; Arlon SQA-TMS-003
	406 microns	16.0 mil	Substrate; Arlon SQA-TMS-003
	711 microns	28.0 mil	Overall; Arlon SQA-TMS-003

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	44	44	Side 2, Layer 2; Compound Property; ASTM D2240
	52	52	Side 1 and Side 2, Layer 1; Compound Property; ASTM D2240
Tensile Strength	6.14 MPa	890 psi	Side 1 and Side 2, Layer 1; Compound Property; ASTM D412
	7.58 MPa	1100 psi	Side 2, Layer 2; Compound Property; ASTM D412
Elongation at Break	550 %	550 %	Side 1 and Side 2, Layer 1; Compound Property; ASTM D412
	650 %	650 %	Side 2, Layer 2; Compound Property; ASTM D412
Peel Strength	3.86 kN/m	22.0 pli	Bond Strength; ASTM D624

Electrical Properties	Metric	English	Comments
Dielectric Strength	19.3 kV/mm	489 kV/in	ASTM D149

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	232 °C	450 °F
Minimum Service Temperature, Air	-56.7 °C	-70.0 °F
UL RTI, Electrical	220 °C	428 °F	E54153
UL RTI, Mechanical without Impact	200 °C	392 °F	E54153

Processing Properties	Metric	English	Comments
Cure Time	15.0 min @Temperature 177 °C	0.250 hour @Temperature 350 °F	Recommended Cure Cycle
	120 min @Temperature 204 °C	2.00 hour @Temperature 400 °F	Recommended Postcure Cycle
Shelf Life	6.00 Month @Temperature 21.1 °C	6.00 Month @Temperature 70.0 °F	From date of manufacture

Descriptive Properties
Color	Red
Total Product Weight (oz/yd²)	31		Arlon SQA-TMS-025

关键词:
供应
硅胶
Arlon 55578R028 0.028" (0.711 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-34044.html

免责声明: 本文 Arlon 55578R028 0.028" (0.711 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络