| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Thickness | 76.2 microns | 3.00 mil | Polyethylene , Interleave | ||
| 330 microns | 13.0 mil | 7500 Fiberglass, Substrate | |||
| 737 - 889 microns | 29.0 - 35.0 mil | Side 1 | |||
| 1070 - 1220 microns | 42.0 - 48.0 mil | Overall | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 50 - 60 | 50 - 60 | Compound Property | ||
| Tensile Strength | 6.21 - 7.58 MPa | 900 - 1100 psi | Compound Property | ||
| Elongation at Break | 450 - 550 % | 450 - 550 % | Compound Property | ||
| Tear Strength | >= 35.1 kN/m | >= 200 pli | |||
| Peel Strength | >= 1.75 kN/m | >= 10.0 pli | Bond Strength | ||
| Compression Set | <= 28 % | <= 28 % | after post cure | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | >= 15.7 kV/mm | >= 400 kV/in | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 30.0 min @Temperature 177 °C | 0.500 hour @Temperature 350 °F | Recommended Cure Cycle | ||
| 240 min @Temperature 204 °C | 4.00 hour @Temperature 400 °F | after 30 minute ramp up cycle, Recommended Postcure Cycle | |||
| Shelf Life | 3.00 Month @Temperature 4.44 °C | 3.00 Month @Temperature 40.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Red | ||||
| Total Product Weight (oz/yd2) | 38.1 - 46.5 | ||||
| Uncoated Fabric Break Strength | 250 lb/in | Fill Direction, Substrate Property | |||
| 300 lb/in | Warp Direction, Substrate Property | ||||