| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Thickness | 76.2 microns | 3.00 mil | Polyethylene, Interleave | ||
| 356 microns | 14.0 mil | Prime Coated 2523 Fiberglass, Substrate | |||
| >= 584 microns | >= 23.0 mil | Side 2 | |||
| 660 microns | 26.0 mil | Side 1 | |||
| 1470 - 1730 microns | 58.0 - 68.0 mil | Overall | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 35 - 45 | 35 - 45 | Compound Property | ||
| Tensile Strength | >= 4.83 MPa | >= 700 psi | Compound Property | ||
| Elongation at Break | >= 300 % | >= 300 % | Compound Property | ||
| Peel Strength | >= 0.877 kN/m | >= 5.00 pli | Bond Strength | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | >= 13.8 kV/mm | >= 350 kV/in | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 177 °C | 0.250 hour @Pressure 50.0 psi, Temperature 350 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 21.1 °C | 6.00 Month @Temperature 70.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Red | ||||
| Total Product Weight (oz/yd2) | 53.1 - 61.5 | ||||
| Uncoated Fabric Break Strength | 350 lb/in | Fill Direction, Substrate Property | |||
| 400 lb/in | Warp Direction, Substrate Property | ||||