| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Thickness | 76.2 microns | 3.00 mil | Polyethylene, Interleave | ||
| 483 microns | 19.0 mil | Prime Coated 7500 Fiberglass, Substrate | |||
| 533 microns | 21.0 mil | Side 2 | |||
| >= 584 microns | >= 23.0 mil | Side 1 | |||
| 1470 - 1730 microns | 58.0 - 68.0 mil | Overall | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 48 - 58 | 48 - 58 | Compound Property, Side 1 | ||
| 52 - 62 | 52 - 62 | Compound Property, Side 2 | |||
| Tensile Strength | >= 0.689 MPa | >= 100 psi | Compound Property, Side 2 | ||
| >= 5.86 MPa | >= 850 psi | Compound Property, Side 1 | |||
| Elongation at Break | >= 300 % | >= 300 % | Compound Property, Side 1 | ||
| >= 500 % | >= 500 % | Compound Property, Side 2 | |||
| Peel Strength | >= 1.40 kN/m | >= 8.00 pli | Bond Strength | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | >= 15.7 kV/mm | >= 400 kV/in | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | ||
| 15.0 min @Pressure 0.689 MPa, Temperature 152 °C | 0.250 hour @Pressure 100 psi, Temperature 305 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 21.1 °C | 6.00 Month @Temperature 70.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Red | ||||
| Total Product Weight (oz/yd2) | 53.2 - 62.6 | ||||
| Uncoated Fabric Break Strength | 250 lb/in | Fill Direction, Substrate Property | |||
| 300 lb/in | Warp Direction, Substrate Property | ||||