- 密度 [g/cm3]: 0.0881
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.0881 g/cc | 0.00318 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Compressive Yield Strength | >= 4.00 MPa | >= 580 psi | Bare, min |
| >= 4.62 MPa | >= 670 psi | Stabilized, min | |
| 5.34 MPa | 775 psi | Bare, typ | |
| 6.14 MPa | 890 psi | Stabilized, typ | |
| Compressive Modulus | 0.448 GPa | 65.0 ksi | Stabilized, typ |
| Shear Modulus | 0.0689 GPa | 10.0 ksi | Plate Shear, L Direction, typ |
| 0.124 GPa | 18.0 ksi | Plate Shear, W Direction, typ | |
| Shear Strength | >= 1.59 MPa | >= 230 psi | Plate Shear, L Direction, min |
| >= 1.76 MPa | >= 255 psi | Plate Shear, W Direction, min | |
| 2.07 MPa | 300 psi | Plate Shear, L Direction, typ | |
| 2.28 MPa | 330 psi | Plate Shear, W Direction, typ | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 177 °C | 350 °F | High strength retained |