- 拉伸强度 [MPa]: 2.3
- 脆化温度 [℃]: -21.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.85 g/cc | 1.85 g/cc | at 25°C |
| Mooney Viscosity | 25 @Temperature 121 °C | 25 @Temperature 250 °F | ML 1+10 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 66 | 66 | Peak value, at 25°C |
| Tensile Strength at Break | 14.5 MPa | 2100 psi | |
| Tensile Strength, Yield | 2.30 MPa @Strain 100 % | 334 psi @Strain 100 % | |
| Elongation at Break | 310 % | 310 % | |
| Tear Strength | 21.6 kN/m | 123 pli | at 25°C |
| Compression Set | 15 % | 15 % | 70 hours at 25°C |
| 10 % @Temperature 100 °C | 10 % @Temperature 212 °F | 70 hours | |
| 12 % @Temperature 175 °C | 12 % @Temperature 347 °F | 70 hours | |
| 22 % @Temperature 200 °C | 22 % @Temperature 392 °F | 70 hours | |
| Thermal Properties | Metric | English | Comments |
| Minimum Service Temperature, Air | -18.0 °C | -0.400 °F | TR test, TR10 |
| -15.5 °C | 4.10 °F | Gehman torsion test, T10 | |
| -8.50 °C | 16.7 °F | Gehman torsion test, T2 | |
| -8.00 °C | 17.6 °F | TR test, TR70 | |
| Brittleness Temperature | -21.0 °C | -5.80 °F | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 160 °C | 320 °F | Cure Measuring Temperature |
| Cure Time | 12.2 min | 0.203 hour | Curelastmeter |